Abstract:This study investigated the durability analysis of geopolymer concrete and conventional concrete specimens, which includes the seawater condition (5% NaCl), sulphate attack (5% sodium sulphate or 5% magnesium sulphate), acid attack (5% sulphuric acid), freezing–thawing, and wetting–drying tests as per the ASTM. In the initial, to make the GPC and conventional concrete mix-design specimens for reference to durability tests. The mass loss, compressive strength, and UPV tests were conducted on both concrete specimens during every durability test after 6 weeks, 12 weeks, 18 weeks, and 24 weeks in seawater condition, sulphate attack, and acid attack, whereas for freeze–thaw and wetting–drying tests were conducted after 30 cycles, 45 cycles, 60 cycles, 75 cycles, and 90 cycles. After immersion in the seawater solution, sodium sulphate solution, and magnesium sulphate for 12 weeks, both concrete specimens were strengthened. However, both concrete specimens degraded continuously after 12 weeks. Thus, the GPC specimens show higher resistance than conventional concrete specimens against for same. The GPC and conventional concrete specimens show that mass losses are 8.1% and 14.2% after 24 weeks of exposure time, respectively, whereas the GPC and conventional concrete specimens retained 56% and 32% compressive strength of original, respectively, after 24 weeks exposure to same. The mass loss of GPC specimens is 7.2% after 90 cycles of freeze–thaw, whereas the conventional concrete specimens show only 2.1% mass loss. The conventional concrete depicts higher strengthening than GPC specimens in the wetting–drying condition. The wetting–drying cycles strengthened the compressive strength of the GPC and conventional concrete specimens, with the GPC and conventional concrete specimens retain 107% and 109% compressive strength of original after 90 wetting–drying cycles, respectively. Among all durability tests, analysis shows that the acid attack is more vulnerable than the other durability test conditions for both GPC and conventional concrete. The GPC specimens are more resistant to durability conditions than OPC concrete specimens.

Durability of low-carbon geopolymer mortar: Different responses to cryogenic attack caused by water content and freeze-thaw mediums

Compositional Dependence of Pore Structure, Strengthand Freezing-Thawing Resistance of Metakaolin-Based Geopolymers

Influence of mixed fibers on fly ash based geopolymer resistance against freeze-thaw cycles

Influence of Water Content on Mechanical Strength and Microstructure of Alkali-Activated Fly Ash/GGBFS Mortars Cured at Cold and Polar Regions

Change of the Coefficient of Thermal Expansion of Mortar Due to Damage by Freeze Thaw Cycles

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Performance Characteristics of Micro Fiber-Reinforced Ambient Cured One-Part Geopolymer Mortar for Repairing

Durability and microstructural evolution of high-performance ecological geopolymer concrete under low-pressure–salt-erosion–freeze–thaw cycling conditions

Chemical–physical–mechanical Stability of MKG Mortars under Sulfate Attacks

Influence of Synthetic Limestone Sand on the Frost Resistance of Magnesium Potassium Phosphate Cement Mortar

Pore Structure as a Response to the Freeze/Thaw Resistance of Mortars

CRYO-DAMAGE OF CEMENTITIOUS MATERIALS SUBJECT TO DIFFERENT FREEZING RATES

Investigation on the Effect of Seawater Condition, Sulphate Attack, Acid Attack, Freeze–Thaw Condition, and Wetting–Drying on the Geopolymer Concrete

Effect of multi-walled carbon nanotubes on durability of high-strength slag-based geopolymer

Study on the Chloride–Sulfate Resistance of a Metakaolin-Based Geopolymer Mortar

Novel approach to microscopic characterization of cryo formation in air voids of concrete

Influence of Freezing Rate on Cryo-Damage of Cementitious Material

Mechanical characteristics and freezing-thawing degradation mechanism for mortar samples under sodium sulfate solutions attack

Potential of Utilizing Form-Stable Phase Change Materials to Improve Freeze–Thaw Resistance of Mortar with Varying Water Content

Analysis of Freeze-Thaw Damage of Cement Mortars Doped with Polyethylene Glycol-Based Form Stable Phase Change Materials

Mechanical Performances and Frost Resistance of Alkali-Activated Coal Gangue Cementitious Materials