Abstract:Herein, ordinary silicate concrete specimens are prepared to study the damage law of a cement-concrete material under the effects of salt erosion and a freeze–thaw environment. NaCl, NaHCO3, and Na2SO4 solutions are separately produced, according to the characteristics of saline soil, to conduct an experimental study on the concrete characteristics during quick salt freezing cycles, and to analyse the changes in its compressive strength, mass loss, and dynamic elastic modulus (DEM) under freeze–thaw cycles. Low-field nuclear magnetic resonance (NMR) and scanning electronic microscopy are used to investigate the change in the microstructure of concrete specimens under salt freeze–thaw cycles (FTCs). The results show the loss in compressive strength, mass, DEM, and NMR spectrum signal increased by 1.5–3 times, 3–5 times, 1.5–2.5 times, and 2–4 times, respectively, for concrete specimens under 50–100 FTCs in 6.8% composite salt solution, in comparison to fresh water. Apparent spalling, decreases in the DEM, and reductions in the compressive strength occur in concrete when increasing the number of salt FTCs. The number of internal cracks in the concrete structure increase under the combined action of salt crystallization, moisture absorption, and freeze–thaw. The changes in the internal microscopic pore volume in concrete structures exhibit the same trend with changes in the macro mechanical properties of concrete. The correlation coefficients between the changes in each peak in the NUR spectrum and the changes in the compressive strength of concrete specimens under FTCs in freshwater or low-concentration salt solutions are both larger than 0.7, calculated using the grey correlation degree method. Therefore, these changes could be used as a potential evaluation index for salt frozen damage to concrete structures.

CRYO-DAMAGE OF CEMENTITIOUS MATERIALS SUBJECT TO DIFFERENT FREEZING RATES

Influence of Freezing Rate on Cryo-Damage of Cementitious Material

Influence of Freezing Rate on the Cryo-Deformation and Cryo-Damage of Cement-Based Materials During Freeze-Thaw Cycles

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Change of the Coefficient of Thermal Expansion of Mortar Due to Damage by Freeze Thaw Cycles

A Study of the Behaviors of Cement-Based Materials Subject to Freezing

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

EXPERIMENTAL RESEARCH ON DEFORMATION BEHAVIOR OF CONCRETE WITH DIFFERENT WATER CONTENTS AFTER CRYOGENIC FREEZE-THAW CYCLES FROM ROOM TEMPERATURE TO -190 ℃

Electrical Response of Mortar Saturated with NaCl Solutions under Freeze–Thaw Cycles

Effect of Supercooling on the Instantaneous Freezing Dilation of Cement-Based Porous Materials

Experimental Study and Mechanism Analysis on Frost Resistance of Normal Performance Concrete under Different Environments

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

Experimental Investigation of the Deformational Behavior of the Interfacial Transition Zone (itz) in Concrete During Freezing and Thawing Cycles

Experimental investigation on electrical response and mechanical performance of cementitious materials at low temperatures

Quantifying Effect of Later Curing on Pores of Paste Subject to Early-Age Freeze-Thaw Cycles by Different Techniques

Effect of freeze–thaw cycles on the stress–strain curves of unconfined and confined concrete

Meso-Scale Failure of Freezing–Thawing Damage of Concrete under Uniaxial Compression

Meso-scale mechanical model for mortar deformation under freeze thaw cycles