Abstract:A one‐pot molten salt electrochemical etching (E) method is proposed to achieve Ti2C MXene directly from elemental substances (Ti, Al, and C), which greatly simplifies the preparation process. By using carbon sources with different morphologies, such as carbon nanotubes and reduced graphene oxide, MAX and MXene with tuned morphology are prepared based on the "carbon‐template‐growth" mechanism. MXenes, a rapidly growing family of 2D transition metal carbides, carbonitrides, and nitrides, are one of the most promising high‐rate electrode materials for energy storage. Despite the significant progress achieved, the MXene synthesis process is still burdensome, involving several procedures including preparation of MAX, etching of MAX to MXene, and delamination. Here, a one‐pot molten salt electrochemical etching (E) method is proposed to achieve Ti2C MXene directly from elemental substances (Ti, Al, and C), which greatly simplifies the preparation process. In this work, different carbon sources, such as carbon nanotubes (CNT) and reduced graphene oxide (rGO), are reacted with Ti and Al micro‐powders to prepare Ti2AlC MAX with 1D and 2D tuned morphology followed by in situ electrochemical etching from Ti2AlC MAX to Ti2CTx MXene in low‐cost LiCl‐KCl. The introduction of the O surface group via further ammonium persulfate (APS) treatment can act in concert with Cl termination to activate the pseudocapacitive redox reaction of Ti2CClyOz in the non‐aqueous electrolyte, resulting in a Li+ storage capacity of up to 857 C g−1 (240 mAh g−1) with a high rate (86 mAh g−1 at 120 C) capability, which makes it promising for use as an anode material for fast‐charging batteries or hybrid devices in a non‐aqueous energy storage application.

Synthesis of fluorine free MXene through lewis acidic etching for application as electrode of proton supercapacitors

MXene-transition Metal Sulfide Composite Electrodes for Supercapacitors: Synthesis and Electrochemical Characterization

Green Synthesis of Fluorine-Free MXene Via Hydrothermal Process: A Sustainable Approach for Proton Supercapacitor Electrodes

Simplified Synthesis of Fluoride-Free Ti 3 C 2 T x via Electrochemical Etching toward High-Performance Electrochemical Capacitors

Synthesis of Fluorine-Free Ti3C2Tx MXenes Via Acidic Activation for Enhanced Electrochemical Applications

In Situ Synthesis of MXene with Tunable Morphology by Electrochemical Etching of MAX Phase Prepared in Molten Salt

HCl-Based Hydrothermal Etching Strategy Toward Fluoride-Free MXenes

Single‐Step Synthesis of Exfoliated Ti3C2Tx MXene through NaBF4/HCl Etching as Electrode Material for Asymmetric Supercapacitor

High capacitance of MXene (Ti3C2T ) through Intercalation and Surface Modification in Molten Salt

A general Lewis acidic etching route for preparing MXenes with enhanced electrochemical performance in non-aqueous electrolyte

One-Pot Green Process to Synthesize MXene with Controllable Surface Terminations using Molten Salts

MXene‐Copper/Cobalt Hybrids Via Lewis Acidic Molten Salts Etching for High Performance Symmetric Supercapacitors

Fluorine-Free Synthesis of High-Purity Ti3 C2 Tx (T=OH, O) via Alkali Treatment

MXenes serving aqueous supercapacitors: Preparation, energy storage mechanism and electrochemical performance enhancement

The fabrication of Ti3C2 and Ti3CN MXenes by electrochemical etching

Tailoring Interlayer Structure and Surface Chemical State Intensifies Redox Reaction Activity of Ti3c2tx Mxene

Fluorine-Free Synthesis of High-Purity Ti3C2Tx (T=OH, O) Via Alkali Treatment

A Facile Etching Route for Preparing Ti 3 C 2 MXene with Enhanced Electrochemical Performance in Silver Nitrate Solution

Electrochemical characterization of Ti3C2T MXene prepared via a molten salt etching route in an acetonitrile-based electrolyte

Intensifying Electrochemical Activity of Ti3C2Tx MXene via Customized Interlayer Structure and Surface Chemistry