Thin Solid Polymer Electrolyte with High‐Strength and Thermal‐Resistant via Incorporating Nanofibrous Polyimide Framework for Stable Lithium Batteries
Zhenxing Wang,Jianqi Sun,Rui Liu,Zhaohu Ba,Jie Dong,Qinghua Zhang,Xin Zhao
DOI: https://doi.org/10.1002/smll.202303422
IF: 13.3
2023-07-30
Small
Abstract:A nanofibrous polyimide (PI) framework‐derived composite electrolyte with a thickness of 17.5 μm is fabricated to ensure good mechanical and electrochemical performances. With the composite electrolyte, the dendrite‐free and favorable cycling performance could be realized and acceptable electrochemical performance is effectuated in LiNi0.5Co0.2Mn0.3O2 (NCM523) solid battery via in situ formation of LiF, N‐species containing electrode/electrolyte interphase. Polyethylene oxide (PEO) based polymer electrolytes show promise in expanding the practical applications of lithium (Li) batteries. However, their applications in Li batteries are usually restricted owing to the lack of mechanical strength, poor oxidative stability, and relatively large thickness. Herein, a nanofibrous polyimide (PI) framework enhanced plasticized‐PEO solid electrolyte is prepared to realize good mechanical and electrochemical performances. Following the configuration with the PI matrix, this "polymer in polymer" composite electrolyte with a thickness of 17.5 μm exhibits enhanced mechanical strength (13.9 MPa) and outstanding thermal stability. Additionally, it preserves the high ionic conductivity (2.25 × 10−4 S cm−1, 25 °C). The Li||Li symmetrical battery with the modified electrolyte could achieve a steady Li plating/stripping of more than 500 h, and the critical current density reaches up to 0.6 mA cm−2 at ambient temperature. The LiFePO4 batteries delivery favorable capacity of 132.2 mAh g−1 with capacity retentions of 96.4% and 85.9% after 500 and 1000 cycles at 1 C, respectively. Acceptable cycling performance also could be achieved in LiNi0.5Co0.2Mn0.3O2 solid batteries via an inorganic‐rich artificial cathode electrolyte interphase.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology