Excellent Performances of Composite Polymer Electrolytes with Porous Vinyl-Functionalized SiO2 Nanoparticles for Lithium Metal Batteries

Hui Zhan,Mengjun Wu,Rui Wang,Shuohao Wu,Hao Li,Tian Tian,Haolin Tang

DOI: https://doi.org/10.3390/polym13152468

IF: 5

2021-07-27

Polymers

Abstract:Composite polymer electrolytes (CPEs) incorporate the advantages of solid polymer electrolytes (SPEs) and inorganic solid electrolytes (ISEs), which have shown huge potential in the application of safe lithium-metal batteries (LMBs). Effectively avoiding the agglomeration of inorganic fillers in the polymer matrix during the organic–inorganic mixing process is very important for the properties of the composite electrolyte. Herein, a partial cross-linked PEO-based CPE was prepared by porous vinyl-functionalized silicon (p-V-SiO2) nanoparticles as fillers and poly (ethylene glycol diacrylate) (PEGDA) as cross-linkers. By combining the mechanical rigidity of ceramic fillers and the flexibility of PEO, the as-made electrolyte membranes had excellent mechanical properties. The big special surface area and pore volume of nanoparticles inhibited PEO recrystallization and promoted the dissolution of lithium salt. Chemical bonding improved the interfacial compatibility between organic and inorganic materials and facilitated the homogenization of lithium-ion flow. As a result, the symmetric Li|CPE|Li cells could operate stably over 450 h without a short circuit. All solid Li|LiFePO4 batteries were constructed with this composite electrolyte and showed excellent rate and cycling performances. The first discharge-specific capacity of the assembled battery was 155.1 mA h g−1, and the capacity retention was 91% after operating for 300 cycles at 0.5 C. These results demonstrated that the chemical grafting of porous inorganic materials and cross-linking polymerization can greatly improve the properties of CPEs.

polymer science

What problem does this paper attempt to address?

The paper aims to address the safety and performance issues faced by lithium metal batteries (LMBs) in practical applications. Specifically, traditional liquid electrolytes pose serious safety hazards such as leakage, flammability, and toxicity, while solid-state electrolytes, although improving safety, still have deficiencies in mechanical and electrochemical performance. The paper proposes a composite polymer electrolyte (CPEs) based on partially cross-linked poly(ethylene oxide) (PEO), by introducing porous vinyl-functionalized silica nanoparticles (p-V-SiO₂) as fillers and using polyethylene glycol diacrylate (PEGDA) as a cross-linking agent. This novel electrolyte combines the mechanical rigidity of inorganic solid electrolytes with the flexibility of organic polymer electrolytes, thereby enhancing the mechanical properties of the electrolyte membrane, effectively inhibiting the recrystallization of PEO, and promoting the dissolution of lithium salts.

Experimental results show that the prepared symmetric Li|CPE|Li cell can operate stably for over 450 hours without short-circuiting, and the all-solid-state Li|LiFePO₄ cell exhibits excellent rate performance and cycling stability. The initial discharge specific capacity reached 155.1 mA h g⁻¹, and after 300 cycles at 0.5 C, the capacity retention rate was 91%, demonstrating that the chemical grafting of porous inorganic materials and cross-linked polymerization can significantly improve the performance of CPEs.