Abstract:The failure of composite laminates under cyclic fatigue loads is complex, as multiple failure mechanisms are in play at different scales and interact with each other. Predicting the remaining fatigue life as well as the residual capacities of a composite laminate or component is crucial, particularly for safety-critical applications. A progressive fatigue model is proposed to describe the catastrophic failure of open-hole laminates under tensile cyclic fatigue. To represent both intra-laminar and inter-laminar damage, a combination of a continuum damage mechanics model (CDM) and a discrete cohesive zone model (CZM) is implemented in the finite element (FE) software Abaqus. The CDM combines fibre- and matrix-dominated S-N curves with the Palmgren–Miner accumulation rule and Hashin’s residual strength to form a fatigue failure criterion differentiating between fibre failure (FF) and matrix failure (MF). The CZM implemented in this work is the CF20 model proposed by NASA. Fatigue cycling is simulated using an external cycle-jump scheme, where the stiffness degradation is conducted between the FE simulations outside of the implicit solver [90/0] s. Glass fibre reinforced polymer (GFRP) open-hole specimens were tested in tensile cyclic fatigue at a load ratio of 0.1. The experiments were reproduced numerically and the results compared. After calibration of a set of parameters based on one load level, the model was able to reproduce the experimental S-N curve very well, predicting a slope of −0.10, while the experimental value was −0.11. The failure sequence of the laminate was also successfully reproduced. The growth of the split from the hole, and its interaction with inter-laminar delamination, was successfully captured. The proposed approach was able to describe the fatigue failure of an open-hole laminate with a minimal set of material inputs using a simplified fatigue damage model while avoiding convergence issues.

Numerical fatigue assessment of a cross-ply carbon fiber laminate using a probabilistic framework

A Methodology to Predict the Fatigue Life under Multi-Axial Loading of Carbon Fiber-Reinforced Polymer Composites Considering Anisotropic Mechanical Behavior

Probabilistic Fatigue Stiffness Variation of Angle-Ply GFRP Composites Considering Stress Ratio Effect

Effect of Stress Ratio and Loading Inclination on the Fatigue Life of Carbon-Fiber-Reinforced Polymer Composites: Multiscale Analysis Approach

Prediction of long-term fatigue life of CFRP composite hydrogen storage vessel based on micromechanics of failure

Numerical Simulation for Durability of a Viscoelastic Polymer Material Subjected to Variable Loadings Fatigue Based on Entropy Damage Criterion

A new data-driven probabilistic fatigue life prediction framework informed by experiments and multiscale simulation

A multi-scale probabilistic methodology to predict high-cycle fatigue lifetime for alloys with process-induced pores

Modeling of progressive high-cycle fatigue in composite laminates accounting for local stress ratios

A Reliable Progressive Fatigue Damage Model for Life Prediction of Composite Laminates Incorporating an Adaptive Cyclic Jump Algorithm

Experimental Study and Modeling of Fatigue Life Prediction of Plain Weave Carbon/Polymer Composite under Constant Amplitude Loading

Fatigue failure mechanism analysis and life prediction of short fiber reinforced polymer composites under tension-tension loading

Multiscale-based multiaxial fatigue model of short fiber reinforced polymer composites under high-cycle proportional loading

A Probabilistic Design Method for Fatigue Life of Metallic Component

A Probabilistic Model for LCF

Fatigue Strength Prediction Of Bolted Joint Structures Of Carbon Fibre Reinforced Polymer Composite Based On The Micromechanics

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates

Probabilistic framework for multiaxial LCF assessment under material variability

Progressive fatigue damage modeling of laminated composites using strain-based failure criteria

Random Fatigue Life Prediction of Carbon Fibre-Reinforced Composite Laminate Based on Hybrid Time-Frequency Domain Method

Fuzzy fatigue life prediction of fiber-reinforced laminated composites by continuum damage mechanics