Abstract:The failure of a component often is the result of a degradation process that originates with the formation of a crack. Fatigue describes the crack formation in the material under cyclic loading. Activation and deactivation operations of technical units are important examples in engineering where fatigue and especially low-cycle fatigue (LCF) play an essential role. A significant scatter in fatigue life for many materials results in the necessity of advanced probabilistic models for fatigue. Moreover, optimization of reliability is of vital interest in engineering, where with respect to fatigue the cost functionals are motivated by the predicted probability for the integrity of the component after a certain number of load cycles. The natural mathematical language to model failure, here understood as crack initiation, is the language of spatio-temporal point processes and their first failure times. The local crack formation intensities thereby need to be modeled as a function of local stress states and thus as a function of the derivatives of the displacement field $u$ obtained as the solution to the PDE of linear elasticity. This translates the problem of optimal reliability in the framework of shape optimization. The cost functionals derived in this way for realistic optimal reliability problems are too singular to be $H^1$-lower semicontinuous as many damage mechanisms, like LCF, lead to crack initiation as a function of the stress at the component's surface. Realistic crack formation models therefore impose a new challenge to the theory of shape optimization. In this work, we have to modify the existence proof of optimal shapes, for the case of sufficiently smooth shapes using elliptic regularity, uniform Schauder estimates, and compactness of strong solutions via the Arzela--Ascoli theorem. This result applies to a variety of crack initiation models and in particular applies to a recent probabilistic model for LCF.

A Probabilistic Model for LCF

Probabilistic Modeling of LCF Failure Times Using an Epidemiological Crack Percolation Model

A Probabilistic Model for Low-Cycle Fatigue Crack Initiation under Variable Load Cycles

An Approach to Estimate the Low Cycle Fatigue Probabilistic Curves of PBF-LB/M 316L Steel from Small Size Datasets Using the Remora Optimization Algorithm

A novel LCF lifetime model for PM superalloys considering crack energy differences induced by surface underconstraint

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

Probabilistic framework for multiaxial LCF assessment under material variability

Probabilistic modeling and simulation of multiple surface crack propagation and coalescence

Optimal Reliability in Design for Fatigue Life

Evaluation of Size Effect in Low Cycle Fatigue for Q&T Rotor Steel

Combined Notch and Size Effect Modeling of Metallic Materials for LCF Using Plasticity Reformulated Critical Distance Theory

Microstructure-based fatigue life model of metallic alloys with bilinear Coffin-Manson behavior

A Novel Energy-Critical Multiaxial Fatigue Life Prediction for Low Cycle Fatigue under Mixed-Mode Loading

High-cycle and low-cycle fatigue life prediction under random multiaxial loadings without cycle counting

A New Method for Low Cycle Fatigue Life Prediction

Probabilistic Analysis of LCF Crack Initiation Life of a Turbine Blade under Thermomechanical Loading

A multi-scale probabilistic methodology to predict high-cycle fatigue lifetime for alloys with process-induced pores

Probabilistic fatigue modelling of metallic materials under notch and size effect using the weakest link theory

Probabilistic Modeling of Fatigue Crack Growth and Experimental Verification

A general energy-based model for fatigue life prediction of high-temperature structural materials

Numerical fatigue assessment of a cross-ply carbon fiber laminate using a probabilistic framework