Abstract:Pure tungsten (W) is generally believed to be a preferred alternative material for kinetic penetrators once a "self-sharpening" effect can be realized by inducing adiabatic shear failure during high-speed impact. However, it is still a major challenge to trigger adiabatic shear bands (ASBs) in pure W with low ductility. In this work, we reported an improved adiabatic shear susceptibility of pure W by controlling the texture evolution during the pre-rolling process. As the rolling strain increased, the texture components and intensity underwent crucial variations to facilitate the appearance of ASBs. For comparative studies, we investigated the dynamic behavior of three kinds of W samples with different microstructural features at a wide range of temperatures (298K∼1473K) via SHPB system, including coarse-grained W (CGW), as-rolled W samples to the thickness reductions of 75% (75W) and 80% (80W). The experimental results revealed a transition of failure behavior from typical brittle fracture to adiabatic shear instability under uniaxial dynamic compression. Of particular interest was that although 75W and 80W exhibited almost the same mechanical properties after the similar rolling reductions, their dynamic instability behaviors differed remarkably with different spatial distributions of texture components. In the as-rolled 75W, two dominant texture components of {001} and {111} were alternate to form fully spaced layers. Under uniaxial compression, the {111} "hard orientation layers" became the obstacles to the propagation of ASBs. Fortunately, in 80W specimens the different {001} "soft orientation layers" were interconnected by the "soft bricks" of the same orientation, which provided pathways for the expansion of shear localization and ultimately the triggering of ASBs. Through subsequent crystal plasticity finite element (CPFEM) simulations, we further verified the effect of orientation distributions on the shear localization and thoroughly explained the formation mechanism of ASBs in the highly textured refractory metal. This may provide guidance for producing advanced materials for certain practical applications.

Anisotropic factors affecting the ductile-brittle transition of rolled‐tungsten after different recrystallization treatments

Effect of Anisotropic Mechanism of W-2%wt Y2O3 Alloy on DBTT and Fracture Analysis under Small Punch Testing

The Influence of Warm Rolling Reduction on Microstructure Evolution, Tensile Deformation Mechanism and Mechanical Properties of an Fe-30Mn-4Si-2Al TRIP/TWIP Steel

Ductile to brittle transition temperature of advanced tungsten alloys for nuclear fusion applications deduced by miniaturized three-point bending tests

The Influence of Crystal Defects on the Elastic Properties of Tungsten Metals

Tailoring the adiabatic shear susceptibility of pure tungsten via texture evolution

High-temperature tensile and thermal shock characterization of low-temperature rolled tungsten

Microstructure and Annealing Behavior of Three Rolled Pure Tungsten Plates with Different Thickness Reduction

Evolution of microstructure and texture of moderately warm-rolled pure tungsten during annealing at 1300 °C

Toughness under Different Rolling Processes in Ultra Purified Fe–17wt% Cr Alloy Steels

Anisotropic behavior of TiB2 nanoparticles reinforced 2024Al composites rolling sheet

Recrystallization behavior of pure tungsten hot-rolled with high accumulated strain during annealing at 1250 C-1350 C

Microstructure, mechanical behaviour and fracture of pure tungsten wire after different heat treatments

Microstructure evolution of the rolled tungsten during the current-assisted annealing treatment

Multiscale crystal plasticity finite element simulations of the deformation inhomogeneity of TiBw/TA15 composites with network-structured during hot rolling

Microstructure and texture evolution in warm-rolled fine-grained tungsten

Effects of Thickness Reduction on Recrystallization Process of Warm-Rolled Pure Tungsten Plates at 1350 °C

Inhomogeneous Deformation Substructure and Its Effect on the Recrystallization Behavior of Yttria Dispersion-Strengthened Tungsten Plate

Microstructural effects on central crack formation in hot cross-wedge-rolled high-strength steel parts

Comparative analysis of cold and warm rolling on tensile properties and microstructure of additive manufactured Inconel 718

Probabilistic and Constitutive Models for Ductile-to-brittle Transition in Steels: A Competition Between Cleavage and Ductile Fracture