Abstract:Pure tungsten (W) is generally believed to be a preferred alternative material for kinetic penetrators once a "self-sharpening" effect can be realized by inducing adiabatic shear failure during high-speed impact. However, it is still a major challenge to trigger adiabatic shear bands (ASBs) in pure W with low ductility. In this work, we reported an improved adiabatic shear susceptibility of pure W by controlling the texture evolution during the pre-rolling process. As the rolling strain increased, the texture components and intensity underwent crucial variations to facilitate the appearance of ASBs. For comparative studies, we investigated the dynamic behavior of three kinds of W samples with different microstructural features at a wide range of temperatures (298K∼1473K) via SHPB system, including coarse-grained W (CGW), as-rolled W samples to the thickness reductions of 75% (75W) and 80% (80W). The experimental results revealed a transition of failure behavior from typical brittle fracture to adiabatic shear instability under uniaxial dynamic compression. Of particular interest was that although 75W and 80W exhibited almost the same mechanical properties after the similar rolling reductions, their dynamic instability behaviors differed remarkably with different spatial distributions of texture components. In the as-rolled 75W, two dominant texture components of {001} and {111} were alternate to form fully spaced layers. Under uniaxial compression, the {111} "hard orientation layers" became the obstacles to the propagation of ASBs. Fortunately, in 80W specimens the different {001} "soft orientation layers" were interconnected by the "soft bricks" of the same orientation, which provided pathways for the expansion of shear localization and ultimately the triggering of ASBs. Through subsequent crystal plasticity finite element (CPFEM) simulations, we further verified the effect of orientation distributions on the shear localization and thoroughly explained the formation mechanism of ASBs in the highly textured refractory metal. This may provide guidance for producing advanced materials for certain practical applications.

Tailoring the adiabatic shear susceptibility of pure tungsten via texture evolution

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Influence of Microstructure on Adiabatic Shear Localization of Pre-Twisted Tungsten Heavy Alloys

Influence of Stress Condition on Adiabatic Shear Localization of Tungsten Heavy Alloys

Microstructure and Annealing Behavior of Three Rolled Pure Tungsten Plates with Different Thickness Reduction

Mechanism of Brittle-to-ductile Transition in Tungsten under Small-Punch Testing

Mechanical Behavior and Dynamic Failure of High-Strength Ultrafine Grained Tungsten under Uniaxial Compression

High susceptibility to adiabatic shear banding and high dynamic strength in tungsten heavy alloys with a high-entropy alloy matrix

Evolution of microstructure and texture of moderately warm-rolled pure tungsten during annealing at 1300 °C

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Effect of Anisotropic Mechanism of W-2%wt Y2O3 Alloy on DBTT and Fracture Analysis under Small Punch Testing

FORMATION MECHENISM OF ADIABATIC SHEAR BAND IN TUNGSTEN HEAVY ALLOYS

High-temperature tensile and thermal shock characterization of low-temperature rolled tungsten

Anisotropic factors affecting the ductile-brittle transition of rolled‐tungsten after different recrystallization treatments

Effect of microtextures on the intermediate temperature fracture behavior of additive-manufactured Ni-based overlay

Microstructure and texture evolution in warm-rolled fine-grained tungsten

Evolution of microstructure and texture in a warm-rolled yttria dispersion-strengthened tungsten plate during annealing in the temperature range between 1200 °C and 1350 °C

Adiabatic shear instability in a titanium alloy: Extreme deformation-induced phase transformation, nanotwinning, and grain refinement

Revealing impact failure behavior of tungsten composite using instrumented Charpy impact testing

Damage Behaviors in Microstructures and Mechanical Properties of Pure Tungsten Induced by Repetitive Thermal Loads

Timely and atomic-resolved high-temperature mechanical investigation of ductile fracture and atomistic mechanisms of tungsten