Fabrication Of Hydrophobic Coatings On Betula Alnoides Wood With Different Alkyltrichlorosilanes

YULAN JIAN,HUI WAN,KAIMENG XU,YARU ZHANG,LINKUN XIE

DOI: https://doi.org/10.1142/S0218625X22501657

2022-12-01

Surface Review and Letters

Abstract:To study the hydrophobic properties of Betula alnoides wood modified by alkyltrichlorosilanes, four alkyltrichlorosilanes with different chain lengths were used to prepare hydrolytic solutions by adding 0.25% (v/v) of alkyltrichlorosilane to anhydrous toluene, and the wood samples were immersed in the hydrolytic solutions for 4h. The surface chemical compositions of the samples were analyzed by X-ray photoelectron spectroscopy (XPS) and Varian 640-IR Fourier Infrared Spectrometer (ATR-FTIR), the surface morphology of the samples was observed by scanning electron microscopy (SEM), and the wettability of the modified wood was investigated using an optical contact angle goniometer. The results demonstrated that treatment with alkyltrichlorosilanes introduced Si and low surface energies of –CH 2 and –CH 3 on the surface of Betula alnoides wood. The –CH 2 and –CH 3 content increased with the increase in chain length. Alkyltrichlorosilanes formed a different micro or nanoscale roughness on the surfaces of the wood samples. The water contact angles of all coatings of alkyltrichlorosilanes are greater than 131.3±2.4∘ , and greater than 115.5±0.9∘ after 180s. The water absorption decreases with the increase in chain length. The water absorption of the uncoated sample is 44.0±1.9 wt.%, while those of samples modified by MTCS and OTCS are 18.0±0.9 wt.% and 11.0±0.0 wt.%, respectively.

chemistry, physical,physics, condensed matter