Abstract:Generally, superhydrophilic self-cleaning coatings are prepared from semiconductors with photocatalytic properties. Organic pollutants attached to the coating surface can be degraded by its photocatalytic performance realizing a self-cleaning goal. Herein, SiO2–TiO2 composite particles were fabricated by the hydrolysis and precipitation of TiOSO4, and SiO2 microspheres were chosen as carriers, which are inexpensive and environmentally friendly. Then, superhydrophilic self-cleaning SiO2–TiO2 coatings were fabricated by spraying the composites on the surfaces of substrates. The morphology, structure and self-cleaning performance of the SiO2–TiO2 coating were characterized and tested. The results revealed that nano-TiO2 was loaded on the surfaces of SiO2 microspheres uniformly forming a hierarchical micro/nanostructure. The SiO2–TiO2 composite particles exhibited excellent photocatalytic degradation performance, and the degradation rate of methyl orange (10 ppm) was more than 98% under UV irradiation for 40 min. Furthermore, the coating prepared with the SiO2–TiO2 composite particles exhibited superhydrophilicity. A water droplet spreads completely on the coating surface in 0.35 s, and the contact angle reaches 0°. In addition, rhodamine B (RhB) and methylene blue (MB) on the coating surface can be degraded efficiently under sunlight irradiation. The SiO2–TiO2 composite particles can be sprayed directly on the surfaces of concrete, brick, wood, and glass slides. Therefore, the particles showed good adaptability to different substrates. The superhydrophilic property was due to the hydrophilicity of SiO2 and TiO2, the hierarchical micro/nanostructure of the SiO2–TiO2 composites, and the photoinduced superhydrophilicity of TiO2. The above experimental results show that the as-prepared superhydrophilic self-cleaning SiO2–TiO2 coating has a large application potential.

Hydrophobicity and Photocatalytic Activity of a Wood Surface Coated with a Fe3+-Doped SiO₂/TiO₂ Film

Hydrophobic Modification of Bi2O3-Doped Si-Ti Composite Film on a Wood Surface

In-situ route for the graphitized carbon/TiO<sub>2</sub> composite photocatalysts with enhanced removal efficiency to emerging phenolic pollutants

Photocatalytic Performance and Kinetic Studies of a Wood Surface Loaded with Bi2O3-Doped Silicon-Titanium Composite Film

Study of Self-Cleaning and Low-Emission Properties of FTO/TiO2 Composite films

Hydrophobic Modification of Wood Using Tetramethylcyclotetrasiloxane

Synthesis of Cu-Doped TiO2 on Wood Substrate with Highly Efficient Photocatalytic Performance and Outstanding Recyclability for Formaldehyde Degradation

Reversible Photocontrol of Wood-Surface Wettability Between Superhydrophilicity and Superhydrophobicity Based on A Tio2 Film

Fabrication of superhydrophilic self-cleaning SiO2–TiO2 coating and its photocatalytic performance

Structure Influence of Fe~(3+)-TiO_(2)/SiO_(2) Film on the Photocatalytic Properties

Photocatalytic Activity and Low-Emissivity Property of Fluorine Doped SnO2/TiO2 Composite Film

Enhanced Photocatalytic Activity for Titanium Dioxide by Co-Modifying with Silica and Fluorine.

Improved weathering performance and wettability of wood protected by CeO2 coating deposited onto the surface

Endowing Three-Dimensional Porous Wood with Hydrophobicity/Superhydrophobicity Based on Binary Silanization

Structure influence of Fe3+ doped TiO2/SiO2 film on the photocatalytic properties

Prolonging the Combustion Duration of Wood by TiO2 Coating Synthesized Using Cosolvent-Controlled Hydrothermal Method

Photo-catalytic activity of Fe3+/Sn4+ co-doped titanium dioxide nano-crystalline thin films for methyl orange degradation

Imparting durable superhydrophobic/oleophobic properties to wood surfaces by means of PFDMS@MTCS vapor deposition

Synergistic Promotion of Photocatalytic Degradation of Methyl Orange by Fluorine- and Silicon-Doped TiO2/AC Composite Material

Photo-Catalytic Activity of Fe3+/Sn4+Co-Doped Titanium Dioxide Nano-Crystalline Thin Films for Methyl Orange Degradation

TiO2 Composite Films on Different Substrates with Enhanced Visible Light Photocatalytic Performance