Abstract:Ultraviolet (UV) light and water have negative effects on the surface appearance of heat-modified wood. Although thermally modified wood is dimensionally more stable than non-modified wood, high temperature and humidity variations may induce some shrinkage and swelling even in the case of modified wood. The results can be formation of cracks on the wood surface. Hence, industries move towards developing clear coats to protect modified wood. In this study, performance of a waterborne polyacrylate coating blended with additives of nanoparticles of TiO2 or ZnO as well as with 2-(2-hydroxyphenyll)-benzotriazole (BTZ) type UV-absorber, and in combination with olive leaf extract or a hindered amine light stabilizer (HALS), was studied. The influence of the mentioned additives on surface roughness and wetting properties, as well as on adhesion strength of coatings on modified thermally modified wood in outdoor exposure was investigated. The coated thermally modified wood samples were exposed to natural weathering for 12 months. In addition, specimens of coated thermally modified wood with the best natural weathering performance were exposed to accelerated weathering. The wettability study results showed that the polyacrylate coating containing TiO2 and olive leaf extract (20%), as well as BTZ and olive leaf extract (10% and 20%) exhibited the best performance during natural weathering. Surface roughness of all coated thermally modified wood was slightly increased after natural weathering. Moreover, the highest adhesion strength was determined at the polyacrylate coating with TiO2 and olive leaf extract (20%) after both natural and accelerated weathering. Thus, a positive influence of a natural antioxidant—olive leaf extract on the weathering performance of polyacrylate wood coating formulations was confirmed.

Improved weathering performance and wettability of wood protected by CeO2 coating deposited onto the surface

Novel two-step strategy for the construction of weathering-resistant hydrophobic wood to extend its service life

Improvement of Water Resistance and Dimensional Stability of Wood Through Titanium Dioxide Coating

Formulation of environmentally robust flame-retardant and superhydrophobic coatings for wood materials

Imparting durable superhydrophobic/oleophobic properties to wood surfaces by means of PFDMS@MTCS vapor deposition

Hydrophobicity and Photocatalytic Activity of a Wood Surface Coated with a Fe3+-Doped SiO₂/TiO₂ Film

Influence of nanoparticles and olive leaf extract in polyacrylate coating on the weathering performance of thermally modified wood

Hydrophobic Modification of Bi2O3-Doped Si-Ti Composite Film on a Wood Surface

Structural study of coated wood with superhydrophobic chitosan/silica hybrid nanocomposite in seawater

UV-Assisted Multiscale Superhydrophobic Wood Resisting Surface Contamination and Failure

Liquidoid Chemical Oxidation Surface Treatment of Polyethylene/Wood Composites

Hydrophobic Modification of Wood Using Tetramethylcyclotetrasiloxane

Weathering performance of thermally modified wood coated with polyacrylate containing olive leaf extract as a bio-based additive

A novel two-step strategy to construct multifunctional superhydrophobic wood by liquid-vapor phase deposition of methyltrimethoxysilane for improving moisture resistance, anti-corrosion and mechanical strength

Fabrication of transparent and durable superhydrophobic polysiloxane/SiO2 coating on the wood surface

One-step Approach to Prepare Superhydrophobic Wood with Enhanced Mechanical and Chemical Durability: Driving of Alkali

Superhydrophobic wood fabricated by epoxy/Cu 2 (OH) 3 Cl NPs/stearic acid with performance of desirable self-cleaning, anti-mold, dimensional stability, mechanical and chemical durability

Reversible Photocontrol of Wood-Surface Wettability Between Superhydrophilicity and Superhydrophobicity Based on A Tio2 Film

In Situ Fabrication of a Superhydrophobic ORMOSIL Coating on Wood by an Ammonia–HMDS Vapor Treatment

Prolonging the Combustion Duration of Wood by TiO2 Coating Synthesized Using Cosolvent-Controlled Hydrothermal Method

The Effect of Antibacterial and Waterproof Coating Prepared From Hexadecyltrimethoxysilane and Nano-Titanium Dioxide on Wood Properties