Abstract:In the modern forestry, the demand for renewable and environmentally friendly wood protection is increasing. This paper reports a green method for preparing stable and self-cleaning superhydrophobic coating for wood protection by dripping polyvinyl alcohol cross-linked hollow silica nanoparticles on the surface of wood in combination with polydimethylsiloxane modification. The coating is based on a laminated structure with layers stacked on the surface of the wood and cured quickly with the assistance of UV. The coatings obtained on wood substrates with appropriate ratios have excellent superhydrophobic properties, with an optimum water contact angle of up to 160.4 ± 0.2°. The coating also exhibits good transparency in the UV-visible spectrum and a maximum transmittance of 91%. With transmission electron microscopy, the microscopic morphology of the self-assembled hollow silica nanoparticles was observed. Scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray diffraction were also applied to investigate the morphology and chemical composition of the coatings. A water contact angle of 151.5 ± 0.7° was maintained even after the abrasion tests with sandpaper at a distance of 300 cm. Meanwhile, the resultant coatings exhibit good self-cleaning properties apart from mechanical durability and chemical stability, which enables effective resistance to contamination. Evidenced by the abovementioned data, this composite coating is capable of optimizing the surface wettability of wood, offering a new dimension to the extensive and prolonged application of wood and wood-based products. Furthermore, considering the advantages of this method, it could also be used in other areas in the future, such as glass, solar substrates, and optical devices.

Preparation of superhydrophobic coatings with alkyltrichlorosilanes for Pinus kesiya wood

Fabrication Of Hydrophobic Coatings On Betula Alnoides Wood With Different Alkyltrichlorosilanes

Role of surface treatment on water absorption of poly(vinyl chloride) composites reinforced by Phyllostachys pubescens particles

Imparting durable superhydrophobic/oleophobic properties to wood surfaces by means of PFDMS@MTCS vapor deposition

Study on the Difference of Superhydrophobic Characteristics of Different Wood Furniture Substrates

Synergetic strategy to fabricate superhydrophobic wood by MTMS for improving dimensional stability, durability and self-cleaning ability

Endowing Three-Dimensional Porous Wood with Hydrophobicity/Superhydrophobicity Based on Binary Silanization

Superhydrophobic wood fabricated by epoxy/Cu 2 (OH) 3 Cl NPs/stearic acid with performance of desirable self-cleaning, anti-mold, dimensional stability, mechanical and chemical durability

A novel two-step strategy to construct multifunctional superhydrophobic wood by liquid-vapor phase deposition of methyltrimethoxysilane for improving moisture resistance, anti-corrosion and mechanical strength

Hydrophobic Modification of Wood Using Tetramethylcyclotetrasiloxane

Fabrication of transparent and durable superhydrophobic polysiloxane/SiO2 coating on the wood surface

Hydrophobic Modification of Bi2O3-Doped Si-Ti Composite Film on a Wood Surface

In Situ Fabrication of a Superhydrophobic ORMOSIL Coating on Wood by an Ammonia–HMDS Vapor Treatment

A transparent superhydrophobic coating on wood-based panel surfaces

A nature-inspired strategy towards superhydrophobic wood

UV-Assisted Multiscale Superhydrophobic Wood Resisting Surface Contamination and Failure

Reversible Photocontrol of Wood-Surface Wettability Between Superhydrophilicity and Superhydrophobicity Based on A Tio2 Film

Novel two-step strategy for the construction of weathering-resistant hydrophobic wood to extend its service life

Green and Abrasion-Resistant Superhydrophobic Coatings Constructed with Tung Oil/Carnauba Wax/Silica for Wood Surface

In-situ growth strategy to fabricate superhydrophobic wood by Na3(Cu2(CO3)3OH)∙4H2O for oil/water separation

Construction of CNC@SiO2@PL Based Superhydrophobic Wood with Excellent Abrasion Resistance Based on Nanoindentation Analysis and Good UV Resistance