Abstract:In this study, the easy moisture absorption of molecular sieves was addressed by a two-step surface hydrophobic modification process. First, the hydrolysis-condensation of tetraethoxysilane (TEOS) was performed on the pre-treated ZSM-5 zeolite powders to fabricate silica encapsulated ZSM-5 (SiO 2 @ZSM-5) molecular sieves. Second, hydrogen-containing silicone oil (HCSO) was grafted on the surface of SiO 2 @ZSM-5 molecular sieves to prepare hydrogen-containing silicone oil modified (HCSO-m-SiO 2 @ZSM-5) nanocomposites. After modification, the BET specific surface area of HCSO-m-SiO 2 @ZSM-5 nanocomposite was reduced from 275 to 69 m 2 ·g −1 , the pore volume was decreased from 0.27 to 0.05 cm 3 ·g −1 , and the average pore diameter was decreased from 4.6 to 2.6 nm. Then, the HCSO-m-SiO 2 @ZSM-5 nanocomposites were used as fillers to endow epoxy resin (EPR) coatings with hydrophobicity. The water contact angle of as-prepared HCSO-m-SiO 2 @ZSM-5/EPR composite coatings reached up to 148° at 30 wt% filler content. Electrochemical analysis shows that the corrosion potential (E corr ) of composite coatings was positively shifted from −1.060 to −0.433 V and the corrosion current (I corr ) was reduced from 9.0791 × 10 −5 to 2.4433 × 10 −6 A/cm 2 with the increase of filler content from 0 to 30 wt%, demonstrating their enhanced anti-corrosion property. Furthermore, the dielectric, light-shielding and mechanical properties were investigated. The results indicate that the composite coatings perform multifunctions of good hydrophobicity, dielectric performance, anti-corrosion, light-shielding efficiency and mechanical properties, which may have great potential in electronics applications.

Tuning the Hydrophobicity of ZSM-5 Zeolites by Surface Silanization Using Alkyltrichlorosilane

Chemical liquid deposition and hydrophobicity of zeolites

Enhanced hydrophobic ZSM-5 with high capacity for toluene capture under high-humidity conditions

Characterization and catalytic activity of silylated nanoscale ZSM-5

Optimization of Conditions for Preparation of ZSM-5@silicalite-1 Core–shell Catalysts Via Hydrothermal Synthesis

EFFECT OF LONG CHAIN CATIONIC SURFACTANT ON ZSM-5 SYNTHESIS AND METHANOL TO OLEFIN REACTION

A Two-Step Organic Modification Strategy for Improving Surface Hydrophobicity of Zeolites

Preparation and Characterization of Amphiphilic HZSM-5 Zeolite with Various Si/Al Ratios

[Preparation of Honeycombed Monolithic Zeolite and Hydrophobic Modification with SiCl4].

Preparation of Amphiphilic HZSM-5 Zeolite by Chemical Vapor Deposition of Trimethylchlorosilane

Effect of Silica Modification on the Shape Selective Adsorption Performance of HZSM-5

Development on hydrophobic modification of aluminosilicate and titanosilicate zeolite molecular sieves

Synthesis and Catalytic Characterization of ZSM-5 Zeolite with Uniform Mesopores Prepared in the Presence of a Novel Organosiloxane

Preparation and study of hydrophobic silica@ZSM-5 nanocomposites for multi-functional coating

Enhanced Hydroisomerization Performance over Highly Mesoporous ZSM-48 Zeolites Constructed by Organosilane Surfactant

Chemical liquid deposition with polysiloxane of ZSM-5 and its effect on acidity and catalytic properties

Fabricating Superhydrophobic and Oleophobic Surface with Silica Nanoparticles Modified by Silanes and Environment-Friendly Fluorinated Chemicals

Optimization of crystal growth of sub-micron ZSM-5 zeolite prepared by using Al(OH)3 extracted from fly ash as an aluminum source

Toluene Disproportionation over ZSM-5 Modified by Silica Deposition and Hydrothermal Treatment

Synthesis of Hydrophobic Zeolite X@SiO2 Core–shell Composites

Optimization and Study of the Response Surface of Properties for the Synthesis of ZSM-5 Zeolites with Hierarchical Pore Structure Obtained by Desilication