Reaction-bonded robust SiC ceramic membranes sintered at low temperature with coal gangue

Yongda Wang,Yuxuan Wang,Pei Nian,Wentao Wang,Dong Wei,Nan Xu,Zhixin Wu,Taotao Zhu,Yibin Wei

DOI: https://doi.org/10.1016/j.ceramint.2023.03.097

IF: 5.532

2023-03-01

Ceramics International

Abstract:Herein, we report an in-situ reaction-bonded SiC membrane sintered at low temperature using a solid waste (i.e. coal gangue) as the sintering aid to form strong neck connections. The effects of sintering temperature and coal gangue proportion on their properties regarding pore size, open porosity, bending strength and pure water permeability were investigated. The single-channel tubular SiC membrane sintered at 1300 °C with a coal gangue proportion of 12 wt% was optimal, exhibiting an average pore size of 2.78 μm, a open porosity of 47.08%, a bending strength of 34.01 ± 1.3 MPa and a high water permeability of 83967 L m−2 h−1 bar−1. The membrane could completely reject D50 = 0.87 μm SiC solids and presented a steady-state water permeability of 458 L m−2 h−1·bar−1. The SiC membrane could be regenerated through ultrasonication and its steady-state water permeability was almost unchanged for 3 cycles, proving its mechanical robustness. This work may appeal to the practical low-cost production of high-performance SiC membranes.

materials science, ceramics