Environment-oriented low-cost porous mullite ceramic membrane supports fabricated from coal gangue and bauxite

Qikai Lü,Xinfa Dong,Zhiwen Zhu,Yingchao Dong

DOI: https://doi.org/10.1016/j.jhazmat.2014.03.026

2014-05-30

Abstract:Porous mullite ceramic supports for filtration membrane were successfully fabricated via recycling of coal gangue and bauxite at sintering temperatures from 1100 to 1500°C with corn starch as pore-forming agent. The dynamic sintering behaviors, phase evolution, shrinkage, porosity and pore size, gas permeation flux, microstructure and mechanical property were systematically studied. A unique volume-expansion stage was observed at increased temperatures from 1276 to 1481°C caused by a mullitization-crystal-growth process. During this stage, open porosity increases and pore size distributions broaden, which result in a maximum of nitrogen gas flux at 1400°C. The X-ray diffraction results reveal that secondary mullitization took place from 1100°C and the major phase is mullite with a content of ∼84.7wt.% at 1400°C. SEM images show that the as-fabricated mullite supports have a porous microstructure composed of sintered glassy particles embedded with inter-locked mullite crystals, which grew gradually with increasing temperature from rod-like into blocky-like morphologies. To obtain mullite membrane supports with sufficient porosity and acceptable mechanical strength, the relationship between porosity and mechanical strength was investigated, which was fitted using a parabolic equation.