Abstract:The erosion behavior of tungsten (W) exposed to low-energy, high flux deuterium (D) plasma has been investigated. The samples were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM) and ion beam analysis (IBA). The eroded thicknesses increase with increasing irradiation fluence from 4.8 × 1025 to 1.64 × 1026 m−2 for 100 eV D plasma bombardment at a temperature of approximately 600 K, however, the corresponding sputtering yields gradually decrease as a function of fluence. A number of possible erosion mechanisms for enhanced sputtering of W by D near the energy threshold which include impurities in the plasma and sample, retained D, surface roughness and morphology, were analyzed. As the sputtering threshold energy predicted by theory and simulation for deuterium on pure W is ∼216 eV and for W with carbon contamination is ∼85 eV, a sputtering yield of 2.32 × 10−6 which was measured for W with only C impurity exposed to a 60 eV deuterium fluence of 1.08 × 1026 m−2 indicates that there were a little amount of impurities such as carbon or oxygen in the D plasma but they show an important contribution to the sputtering yield of the W under 100 eV D plasma erosion. The C impurity in the sample can significantly enhance the sputtering yield of W through increasing energy transfer efficiency in a triple collision cascade system, and the change of C concentration from 14 at.% at the surface to 5.6 at.% in the deeper region of the sample dominates the change of erosion rate under 100 eV plasma bombardment. It is recommended to reducing the impurity concentration to very low levels, whether from background D plasma or contaminants in the near-surface of W wall, will be very beneficial for decreasing W erosion in Tokamak operation.

The erosion and retention properties of tungsten trioxide films exposed to low energy deuterium ions: Temperature dependence

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Deuterium behavior in tungsten exposed to deuterium plasma with rising or declining temperature

Dependence of deuterium retention and surface blistering on deuterium plasma exposure temperature and fluence in lanthanum oxide doped tungsten

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation

Surface morphology and deuterium retention in tungsten exposed to high flux D plasma at high temperatures

The influence of impurities on the erosion of tungsten by low energy high flux deuterium plasma irradiation

Deuterium Retention in Tungsten Films Deposited by Magnetron Sputtering

Effects of Tantalum Alloying on Surface Morphology and Deuterium Retention in Tungsten Exposed to Deuterium Plasma

Effect of initial exposure temperature on the deuterium retention and surface blistering in tungsten

Nanostructure Evolution and Surface Modification of Tungsten Exposed to Low Energy, High Flux Deuterium Plasma

Deuterium Blistering in Tungsten and Tungsten Vanadium Alloys

Influence of Surface Melting on the Deuterium Retention in Pure and Lanthanum Oxide Doped Tungsten

Surface blistering and deuterium retention behaviors in pure and ZrC-doped tungsten exposed to deuterium plasma

Surface modification and deuterium retention in hot-rolled potassium doped tungsten alloy exposed to deuterium plasma

Surface modification and deuterium retention of tungsten and tungsten-rhenium alloys exposed to deuterium plasma

TEM Studies of 1 MeV Fe+ Ion-Irradiated W Alloys by Wet Chemical Method: High-Temperature Annealing and Deuterium Retention

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Tungsten fuzz annealing effect on deuterium retention in polycrystalline tungsten

Microstructure Evolution and Effect on Deuterium Retention in TiC- and ZrC-Doped Tungsten under He+ Ion Irradiation

Deuterium retention and transport in ion-irradiated tungsten exposed to deuterium atoms: role of grain boundaries