Dual-phase synergetic precipitation in Nb/Ta/Zr co-modified Fe–Cr–Al–Mo alloy
Ben Niu,Zhenhua Wang,Qing Wang,Qianfu Pan,Chuang Dong,Ruiqian Zhang,Huiqun Liu,Peter K. Liaw,Wei Xu
DOI: https://doi.org/10.1016/j.intermet.2020.106848
IF: 4.075
2020-09-01
Intermetallics
Abstract:<p>The present work investigated the synergetic effect of Nb/Ta/Zr co-alloying on the microstructural stability of precipitates in the body-centered-cubic (BCC) matrix at high temperatures in Fe-13.5Cr-4.7Al-2.1Mo-0.5Nb-0.8Ta-0.2Zr (wt. %). Alloy plates were fabricated by vacuum arc melting and multi-pass hot rolling, then aged at 1073 K for 24 h, and finally re-treated at different temperatures (1273–1473 K) for 1 h to study the re-dissolution of precipitates. A large amount of Fe<sub>2</sub>M (M = Mo,Nb,Zr,Ta) Laves phase particles with a high-entropy effect were dispersed on BCC matrix with a volume fraction of <em>f</em> ~ 4.6% in 1073 K-aged alloy. These particles were then coarsened and dissolved into matrix obviously after high temperatures re-treatments, as evidenced by the amount of particles with <em>f</em> ~ 0.7% at 1473 K. More importantly, this value is about ten times higher than that in alloys without Zr addition (<em>f</em> ~ 0.05%), in which these particles are still distributed both in inner grains and on grain boundaries. The higher microstructural stability at high temperatures is ascribed to the co-precipitation of Fe<sub>2</sub>M, Fe<sub>23</sub>Zr<sub>6</sub>, and core(Fe<sub>23</sub>Zr<sub>6</sub>)-shell(Fe<sub>2</sub>M)-structured particles, rather than Laves phase alone. The mechanical property of this alloy at both room and high temperatures was also studied.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering