Abstract:The room-temperature strength of Al0.3CoCrFeNi high-entropy alloys (HEAs) is relatively low owing to its intrinsic fcc structure. In the present study, the as-cast HEAs were subjected to cold rolling and subsequent annealing treatment (800, 900, and 1000 °C) to adjust the microstructures and tensile properties. This treatment process resulted in the partial recrystallization, full recrystallization, and grain coarsening with increasing the annealing temperature. It was found that the large and spherical B2 precipitates were generated in the recrystallized grain boundaries of three annealing states, while the small and elongated B2 precipitates were aligned along the deformation twins in the non-recrystallized region of the 800 °C-annealing state. The former B2 precipitates assisted in refining the recrystallized grains to quasi ultra-fine grain and fine grain regimes (with the grain sizes of ~0.9, ~2.2, and ~7.2 μm). The tensile results indicated that the decreased annealing temperature induced the gradual strengthening of this alloy but also maintained the ductility at the high levels. The yield strength and ultimate tensile strength in 800 °C-annealed specimen were raised as high as ~870 and ~1060 MPa and the ductility was maintained at ~26%. The strengthening behavior derived from the heterogeneous microstructures consisting of quasi ultra-fine recrystallized grains, non-recrystallized grains, deformation twins, dislocations, and B2 precipitates. Current findings offer the guidance for designing the HEAs with good strength and ductility.

High-strength and energetic Al2Ti6Zr2Nb3Ta3 high entropy alloy containing a cuboidal BCC/B2 coherent microstructure

Experimental and DFT Investigations of AlNbTiVZr High Entropy Alloys with Excellent Mechanical Properties

Microstructure, Mechanical Properties and Energetic Characteristics of a Novel High-Entropy Alloy HfZrTiTa0.53

Microstructural Evolutions and Mechanical Properties of Energetic Al1 (TiZrNbTaMoCr)15 High-Entropy Alloys

Formation of coherent BCC/B2 microstructure and mechanical properties of Al–Ti–Zr–Nb–Ta–Cr/Mo light-weight refractory high-entropy alloys

A Novel High-Entropy Alloy with Exceptional Strength and Elongation Via Bimodal Grains and Lamellar Nano-Precipitates

High specific yield strength TiZrAlNbV high-entropy alloys via coherent nanoprecipitation strengthening

Improving mechanical properties of an FCC high-entropy alloy by γ′ and B2 precipitates strengthening

Multicomponent Ni-rich High-Entropy Alloy Toughened with Irregular-Shaped Precipitates and Serrated Grain Boundaries

Novel Metastable Engineering in Single-Phase High-Entropy Alloy

Microstructure and mechanical properties of the TiZrNbMoTa refractory high-entropy alloy produced by mechanical alloying and spark plasma sintering

The Microstructures, Mechanical Properties, and Deformation Mechanism of B2-Hardened NbTiAlZr-Based Refractory High-Entropy Alloys

Deformation Behavior and Microstructure Evolution of As-Cast Ti2ZrMo0.5Nb0.5 High Entropy Alloy

Mechanical properties and impact energy release characteristics of Al0.5NbZrTi1.5Ta0.8Ce0.85 high-entropy alloy

High-temperature structural and mechanical stability of refractory high-entropy alloy Nb40Ti25Al15V10Ta5Hf3W2

Microstructure, Phase Stability and Mechanical Properties of Nb–Ni–Ti–Co–Zr and Nb–Ni–Ti–Co–Zr–Hf High Entropy Alloys

Formation mechanism of AlNbTiVZr high entropy alloy/Ti multi-principal element alloy by laser direct energy deposition: Microstructure evaluation and mechanical properties

Microstructural Evolution and Tensile Properties of Al0.3CoCrFeNi High-Entropy Alloy Associated with B2 Precipitates

A hypoeutectic high-entropy alloy with hierarchical microstructure for high-temperature application

Microstructural evolution and mechanical behavior of novel Ti1.6ZrNbAl lightweight refractory high-entropy alloys containing BCC/B2 phases

Precipitation-hardened High Entropy Alloys with Excellent Tensile Properties