High-throughput preparation and quick characterization of oxidation behaviors of complex Al–Cr compositional gradient coatings on a novel Co–Al–W–based superalloy prepared using multi-arc ion plating technology

Q. Guan,X.H. Guo,L.L. Fan,B.L. Meng,J.B. Sha

DOI: https://doi.org/10.1016/j.intermet.2024.108464

IF: 4.075

2024-08-27

Intermetallics

Abstract:The early oxidation behaviors of complex Al–Cr compositional gradient coatings on a novel Co–Al–W substrate prepared by multi-arc ion plating technology (MIPT) at 1000 °C for 20–60 min were rapidly characterized. The as-deposited coatings with compositions ranging from (55%–90%Al, 45%–10%Cr) exhibited the laminated structure α-Al + Al 80 Cr 20 +Al 8 Cr 5 +α-Cr. After annealing at 640 °C for 40 h, a two-layered coating composed of (Co(Al, Cr) + Al 8 Co 18 Cr 4 ) and IRL formed, and the thickness of the coating increased from the 14–18 μm of the as-deposited state to 25–35 μm. During oxidation at 1000 °C for 20–60 min, a three-layer structure consisting of an outer α-Al 2 O 3 +α-Cr 2 O 3 +CoCr 2 O 4 layer, a central unoxidized Al–Cr layer, and an inner μ-Co 7 (W 0.55 Cr 0.45 ) 6 +B 2 –CoAl layer formed on the substrate. The Al–Cr coatings with higher Cr content had a looser oxide layer due to the CoCr 2 O 4 phase, which might degrade the intended protective effect of the Al–Cr coatings. Thus, the Al–Cr coatings with higher Al content were suitable for preventing oxidation behavior. This work proposes a high-throughput screening method for rapid characterization of the early oxidation mechanism of the complex Al–Cr compositional gradient coatings.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering