Abstract:Doped ceria has been extensively explored as an efficient electrolyte material for intermediate to low temperature solid oxide fuel cell. Among other ceria electrolytes, gadolinia doped ceria (GDC) is one of the most extensively studied electrolyte materials for low temperature SOFC applications. Here, co-precipitation method is employed to synthesize GDC nanoparticles with stoichiometric ratio of Gd x Ce 1−x O 2−δ (with 0 x 0.20). In this process, the molecular water of the precursors has been utilized during the co-precipitation to avoid possible agglomeration caused by hydrogen bonding. The cubic phase formation was examined using X-ray diffraction (XRD) and Raman profile ascribing absence of other phases. XRD along with Reitveld refinement confirm the presence of cubic phase of ceria and Raman profile confirms the oxygen vacancies due to the non-stoichiometry created in CeO 2 lattice. The granularity of the sample was observed using field emission scanning electron microscopy (FESEM) with elemental mapping by EDS. It is observed from FESEM that the grains are compact in nature and the density observed was around 98% of the theoretical density. The electrochemical behavior was investigated using electrochemical impedance spectroscopy (EIS), which was taken between the temperature ranges of 350–700 °C. It is observed from the EIS study that ceria doped with 15 mol % Gd 3+ (Gd 0.15 Ce 0.85 O 2−δ ) is having highest grain boundary ionic conductivity of about 0.104 S cm −1 at 700 °C with an activation energy of 0.81 eV. This work demonstrates the correlation between oxygen vacancy generation and the enhancement of ionic conductivity with Gd 3+ doping in ceria.

Effect of cold sintering process (CSP) on the electro-chemo-mechanical properties of Gd-doped ceria (GDC)

Improved densification in cold sintering of gadolinia‐doped ceria with reactive sintering aids

Sintering behavior and electrical conductivity of Ce0.9Gd0.1O1.95 powder prepared by the gel-casting process

Study on Agglomeration and Densification Behaviors of Gadolinium-Doped Ceria Ceramics

Ultrafast high-temperature sintering of gadolinia-doped ceria

Effect of oxygen defects blocking barriers on gadolinium doped ceria (GDC) electro-chemo-mechanical properties

Sintering of Samarium-doped ceria powders prepared by a glycine-nitrate process

Effect of cold sintering on the sintering shrinkage matching of NiO-GDC anode with GDC electrolytes in making anode-supported solid oxide fuel cells

Cold Sintering Process for ZrO2‐based Ceramics: Significantly Enhanced Densification Evolution in Yttria‐doped ZrO2

Annealing of Gadolinium-Doped Ceria (GDC) Films Produced by the Aerosol Deposition Method

Demonstration of the cold sintering process study for the densification and grain growth of ZnO ceramics

Effects of Sintering Parameters on the Low-Temperature Densification of GDC Electrolyte Based on an Orthogonal Experiment

Cold Sintering: A Paradigm Shift for Processing and Integration of Ceramics

The Effects of Cold Sintering Parameters on the Densification of Na2WO4 Ceramics Using Na2WO4·2H2O Dry Powders

Cold sintering of ceria-based solid electrolyte with the assistance of a core-shell structure

Electrical Properties of Ce0.8Gd0.2O1.9 Ceramics Prepared by an Aqueous Process

Cold sintering process of Li 1.5 Al 0.5 Ge 1.5 (PO 4 ) 3 solid electrolyte

Gd-doped ceria with extraordinary oxygen-ion conductivity for low temperature solid oxide fuel cells

Influence of Cold Sintering Process on the Structure and Properties of Garnet-Type Solid Electrolytes

Influence of Lithium Oxide Addition on the Sintering Behavior and Electrical Conductivity of Gadolinia Doped Ceria

Effects of In-Air Post Deposition Annealing Process on the Oxygen Vacancy Content in Sputtered GDC Thin Films Probed via Operando XAS and Raman Spectroscopy