Abstract:In the past decades, Zirconia (ZrO2) has emerged as a promising technical ceramic, both as high temperature structural material and electrolyte for fuel cells, etc. The traditional synthesis of ZrO2 with spark plasma sintering (SPS) usually requires a sintering temperature as high as 1200 °C. General interest in lowering the sintering temperature to reduce energy consumption and thermal stresses has led to research on two promising routes – cold sintering via temperature-dependent chemical reactivity and sintering aids, which facilitates mass transport and improves densification. Here we combine both by developing a single-step sintering process benefitting from both water vapor through the in-situ conversion of Zr(OH)4 to ZrO2 and liquid phase Bi2O3 as a sintering aid. The resultant ZrO2 has a relative density above 80% with a sintering temperature as low as 900 °C, significantly higher than that of ZrO2 without sintering aids, which had a relative density of 54%, both sintered at 50 MPa. The dependence of porosity of sintered samples as a function of sintering pressure (range: 50 MPa–300 MPa) and temperature (range 400 °C–1200 °C) is mapped out as guidance for further material property design. A linear relationship between hardness and relative density was found, with a maximal hardness of 6.6 GPa achieved in samples with 30% porosity. In addition to sintered density, phase stabilization of tetragonal ZrO2 is enhanced at sintering temperature of 900 °C with water vapor and Bi2O3, respectively.

Improved densification in cold sintering of gadolinia‐doped ceria with reactive sintering aids

Study on Agglomeration and Densification Behaviors of Gadolinium-Doped Ceria Ceramics

Effect of cold sintering process (CSP) on the electro-chemo-mechanical properties of Gd-doped ceria (GDC)

Improved Mechanical Properties of 3YSZ Ceramics Prepared by Pressure-less Sintering Assisted by Cold Sintering under Mild Conditions

Sintering behavior and electrical conductivity of Ce0.9Gd0.1O1.95 powder prepared by the gel-casting process

Effect of agglomeration on the densification properties of Sm0.15Gd0.05Ce0.8O1.9 electrolytes for intermediate temperature solid oxide fuel cells

Cold sintering of ceria-based solid electrolyte with the assistance of a core-shell structure

DFT Investigations on Sintering Behavior of Gadolinia-Doped Ceria with Lithium Oxide Additives

Sintering of Ce0.8Sm0.2O1.9

Sintering of Ce（0.8）Sm（0.2）O（1.9）

Influence of Lithium Oxide Addition on the Sintering Behavior and Electrical Conductivity of Gadolinia Doped Ceria

Influence of bismuth oxide as a sintering aid on the densification of cold sintering of zirconia

Effects of Sintering Parameters on the Low-Temperature Densification of GDC Electrolyte Based on an Orthogonal Experiment

Evaluation of Li2O As an Efficient Sintering Aid for Gadolinia-Doped Ceria Electrolyte for Solid Oxide Fuel Cells

Dense SiC ceramics prepared by using amorphous sintering additives

Highly Active Sm0.2Ce0.8O1.9 Powders of Very Low Apparent Density Derived from Mixed Cerium Sources

Thermal-assisted cold sintering study of Al2O3 ceramics: Enabled with a soluble γ-Al2O3 intermediate phase

Doped Ceria Electrolyte Powders Of High Sinterability Synthesized By Glycine-Nitrate Process

A novel two-step cold sintering process to fabricate dense ZnO nanocrystalline ceramics

Dense gypsum ceramics prepared by room-temperature cold sintering with greatly improved mechanical properties

Microstructural evolution of ZnO via hybrid cold sintering/spark plasma sintering