Characteristics of Li2CO3 as sintering aid for Ce0.8Sm0.2O2−δ electrolyte in solid oxide fuel cells
Gwang Seon Park,Su In Mo,Jun Ho Kim,Jeong Woo Yun
DOI: https://doi.org/10.1007/s11814-022-1112-5
IF: 2.7
2022-05-05
Korean Journal of Chemical Engineering
Abstract:Owing to its excellent ionic conductivity, 20 mol% samarium doped ceria (Ce 0.8 Sm 0.2 O 2− δ , SDC) is considered a promising alternative as an electrolyte in solid oxide fuel cells (SOFCs). SDC electrolytes, however, require high sintering temperatures over 1,600 °C to attain sufficient density to be SOFC electrolytes. To lower the SDC sintering temperature, different amounts of Li 2 CO 3 (0–12 mol% of Li) were evaluated as a sintering aid for SDC electrolytes. The SDC electrolyte samples with Li were sintered at 1,400 °C and were compared with SDC electrolytes sintered at 1,600 °C. The SDC electrolyte with 6 mol% of Li sintered at 1,400 °C (Li6SDC1400) was densified to 97.495% of theoretical density (T.D.), which is similar to that achieved by the SDC electrolyte sintered at 1,600 °C (97.433% of T.D.). The improved formation of grain boundary in the Li6SDC1400 sample increased the density of the SDC, resulting in enhancement of ionic conductivity and cell performance. At 800 °C, the maximum power density of the Li6SDC1400 electrolyte sample was 120.15 mW/cm 2 .
engineering, chemical,chemistry, multidisciplinary