Multi-functional superhydrophobic coatings on mg Li alloys via SiO 2 nano particles assembled surface modification
Siyuan Jin,Zhou Jie,Ruizhi Wu,Xiaochun Ma,Mengyao Pang,Zhe Yu,Wang Guixiang,Jinghuai Zhang,Boris Krit,Sergey Betsofen,Vitalii Neshchimenko,Buzikov Ruslan,Min Qiu,Yurong Yang,Jiaming Chen
DOI: https://doi.org/10.1016/j.surfcoat.2024.131568
IF: 4.865
2024-11-23
Surface and Coatings Technology
Abstract:A multi-structured composite coating with superhydrophobic properties, corrosion resistance, and wear resistance was prepared on the surface of Mg-9Li-3Al alloy. A porous layer was formed on the substrate surface via micro-arc oxidation. Then, LDH was grown in situ on the MAO coating surface through hydrothermal treatment, sealing the pores in the coating. Finally, HDTMS-SiO2 was assembled on the LDH surface. The SiO2 formed an island-like micro-nano structure, trapping air and creating an "air cushion" on the coating surface,imparting superhydrophobicity (contact angle and sliding angle of 162.1 ± 2.1° and 4.2 ± 0.2°). And the corrosion resistance of the MLS coating is significantly improved the corrosion current density decreased by three orders of magnitude. The incorporation of HDTMS-SiO2 not only improved the corrosion resistance of the coating but also significantly enhanced its wear resistance. During friction, the SiO2 nanoparticles acted as "ball bearings," shifting the friction mode from sliding to rolling. The fragmented SiO2 further served as a solid lubricant, reducing the coefficient of friction to 0.11.
physics, applied,materials science, coatings & films