Abstract:A one-step electrodeposition method was developed to simultaneously prepare multifunctional superhydrophobic/ superoleophilic coatings on cathodic and anodic magnesium surfaces, which was conducted in an ethanol solution containing magnesium nitrate and myristic acid. The morphology, wettability and chemical composition were characterized, which indicated that the low surface energy material (magnesium myristate) and hierarchical structures were generated on surfaces of the anode and cathode during this process. Water contact angles (CAs) of the coatings were greater than 150 degrees and sliding angles (SAs) were less than 6 degrees. Moreover, contact angles of olive oil, benzene, methylbenzene and dichloromethane were 0 degrees. The corrosion potentials (E-corr) of the anodic and cathodic superhydrophobic/ superoleophilic coatings increased and corrosion current density (i(corr)) decreased by 2 orders of magnitude, showing excellent corrosion resistance. Oil absorption tests showed that the superhydrophobic and superoleophilic property remained and the oil absorption capacities of the prepared coatings were 4.65 g/g and 7.62 g/g respectively even after 10 times of oil absorption and deoiling. Moreover, the anodic and cathodic superhydrophobic/ superoleophilic coatings exhibited outstanding self-cleaning ability, chemical, long-term storage and mechanical stabilities. Since the substrates are bulk materials, this method may have a promising future in enlarging the applications of magnesium alloys. C) The Author(s) 2016. Published by ECS. All rights reserved.

Electroplated super-hydrophobic Zn-Fe coating for corrosion protection on magnesium alloy

Facile formation of super-hydrophobic nickel coating on magnesium alloy with improved corrosion resistance

Preparation and properties of super-hydrophobic coating on magnesium alloy

Facile fabrication of robust superhydrophobic coating for enhanced corrosion protection on AZ91 magnesium alloy by electroless Ni-B/GO plating

One-Step Electrodeposition Process to Fabricate Corrosion-Resistant Superhydrophobic Surface on Magnesium Alloy

Fabrication of Corrosion-Resistant Superhydrophobic Coating on Magnesium Alloy by One-Step Electrodeposition Method

Fabrication of a super-hydrophobic surface on a magnesium alloy by a simple method

Fabrication of Stable Superhydrophobic Surface with Improved Anticorrosion Property on Magnesium Alloy

One-Step Electrodeposition Process to Fabricate Superhydrophobic Surface with Improved Anticorrosion Property on Magnesium Alloy

Eco-Friendly Superhydrophobic Coupling Conversion Coating with Corrosion Resistance on Magnesium Alloy.

Preparing Superhydrophobic Nanocomposite Coating with SiO2 Nanoparticles on Magnesium Alloy

Harnessing superhydrophobic coatings for enhancing the surface corrosion resistance of magnesium alloys

Fabrication of superhydrophobic needle-like Ca-P coating with anti-fouling and anti-corrosion properties on AZ31 magnesium alloy

Fabrication of Corrosion Resistant Superhydrophobic Surface with Self-Cleaning Property on Magnesium Alloy and Its Mechanical Stability

Hydrophobic Modification of Magnesium Hydroxide Coating Deposited Cathodically on Magnesium Alloy and Its Corrosion Protection

One-step Fabrication of Biomimetic Superhydrophobic Surface by Electrodeposition on Magnesium Alloy and Its Corrosion Inhibition

Superhydrophobic Corrosion-Resistant Coating of AZ91D Magnesium Alloy: Preparation and Performance

Formation of a Hydrophobic and Corrosion Resistant Coating on Magnesium Alloy Via a One-Step Hydrothermal Method

Silica nanoparticles enhanced polysiloxane-modified nickel-based coatings on Mg alloy for robust superhydrophobicity and high corrosion resistance

Simultaneously Fabricating Multifunctional Superhydrophobic/Superoleophilic Coatings by One-Step Electrodeposition Method on Cathodic and Anodic Magnesium Surfaces

Electrodeposition of Peony Flower-Like Structure Surface with Self-Cleaning and Anti-corrosion Properties