Surface Defect Passivation and Energy Level Alignment Engineering with a Fluorine-Substituted Hole Transport Material for Efficient Perovskite Solar Cells

Li Tao,Biyi Wang,Haoxin Wang,Cheng Chen,Xingdong Ding,Yi Tian,Hongfei Lu,Xichuan Yang,Ming Cheng

DOI: https://doi.org/10.1021/acsami.0c21975

2021-03-11

Abstract:The surface and boundary defects present in the perovskite film are reported to be nonradiative recombination and degradation centers, restricting further improvement of the power conversion efficiency (PCE) and long-term stability of perovskite solar cells. To address this problem, herein, we introduce a fluorine-substituted small molecular material 2FBTA-1 as a bifunctional buffer layer to efficiently passivate the surface defects of perovskite and tune the energy level alignment between the perovskite/2,2′,7,7′-tetrakis(<i>N</i>,<i>N</i>-di-(<i>p</i>-methoxyphenyl)amino)-9,9′-spirobifluorene (Spiro-OMeTAD) interface. X-ray photoelectron spectroscopy shows that with the insertion of 2FBTA-1 between perovskite and Spiro-OMeTAD, the metallic Pb⁰ defects and uncoordinated Pb²⁺ defects are well restricted. Consequently, the average PCE is distinctly improved from 18.4 ± 0.51 to 20.3 ± 0.40%. Moreover, the long-term stability of unencapsulated devices with 2FBTA-1 treatment under ambient conditions (relative humidity 40–60%) is effectively enhanced, retaining 87% of the initial efficiency after storage for 500 h.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c21975?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c21975</a>.Enlarged image of XRD patterns, UV–vis absorption spectra and UPS measurement of the perovskite film w/ and w/o 2FBTA-1, IR spectra of PbI₂ w/ and w/o 2FBTA-1 treatment, and cross-sectional SEM image of 2FBTA-1-treated PSC (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c21975/suppl_file/am0c21975_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology

What problem does this paper attempt to address?

This paper aims to solve two main problems in perovskite solar cells:

1. **Surface and interface defects**: The surface and boundary defects existing in perovskite films have been reported as non - radiative recombination centers and degradation centers, which limit the power conversion efficiency (PCE) and long - term stability of perovskite solar cells (PSCs). These defects cause unnecessary recombination of charges during the transmission process, thus reducing the performance of the cells.

2. **Energy level alignment problem**: The energy level mismatch between perovskite and hole - transport materials (HTM) is also a key issue. In particular, the highest occupied molecular orbital (HOMO) energy level of the commonly used HTM material Spiro - OMeTAD is too high, and there is a large energy difference between it and the valence band (VB) of perovskite, which affects the hole extraction efficiency and leads to high voltage losses.

To solve these problems, the author introduced a fluorinated small - molecule material 2FBTA - 1 as a buffer layer, which has the following functions:

- **Surface defect passivation**: By inserting 2FBTA - 1 between perovskite and Spiro - OMeTAD, the metal Pb0 defects and uncoordinated Pb2+ defects are effectively limited, reducing non - radiative recombination and ion migration.

- **Energy level regulation**: The introduction of 2FBTA - 1 constructs a cascaded energy level arrangement, reducing the energy level gap between perovskite and Spiro - OMeTAD and improving the hole extraction and transmission efficiency.

The experimental results show that the average PCE of PSCs treated with 2FBTA - 1 increased from 18.4% to 20.3%, and the unpackaged devices still maintained 87% of the initial efficiency after aging for 500 hours under environmental conditions with a relative humidity of 40% - 60%. These results indicate that 2FBTA - 1 not only improves PCE but also significantly enhances the long - term stability of PSCs.