Abstract:Indentation fracture is a commonly employed technique for investigating solids' material properties and response to indentation. Subsurface lateral cracks are related to the mass lost on materials presenting brittle behaviour, and these cracks are usually observed in indentation experiments performed above critical loads. In this study, five microindentations were superimposed to evaluate the formation of lateral cracks under low loads, lower than the critical load, on soda-lime glass. Experimental tests were carried out using a standard Vickers indenter for individual indentations, revealing that radial cracks appeared for indentation forces greater than 98 mN. In comparison, lateral cracks only manifested for indentation forces exceeding 980 mN. To further investigate this phenomenon, we performed superimposition tests, consisting of seven lines, each containing five indentations. The indentation load ranged from 200 to 1000 mN, with varying relative distances between indentations in subsequent lines, thereby controlling the superimposition index from − 200 to 90%. Our findings established a direct correlation between crack formation, the degree of superimposition, and the indentation load. A single indentation performed with a load below the critical threshold did not generate sufficient stress to initiate lateral crack formation. However, with the superimposition of indentations, the interaction of the residual stress field near the previous indentation imprints induced lateral cracks even with loads five times lower than the critical threshold. These insights contribute to a deeper understanding of the mechanics involved in indentation-induced crack formation in brittle materials, with potential implications for material science and engineering applications.

Surface damage resistance and yielding of chemically strengthened silicate glasses: From normal indentation to scratch loading

Hardness and scratch resistance of chemically strengthened alkali‐borosilicate thin glass

Size-Dependent Brittle-To-Ductile Transition in Silica Glass Nanofibers

Scratch test of soda-lime glass

The Competing Effect of Initial Crack Depth Versus Chemical Strengthening Parameters on Apparent Fracture Toughness of Sodium Aluminosilicate Glass

Revealing the surface structural cause of scratch formation on soda-lime-silica glass

Soft Impact Response of Laminated Glass Plates

Influence of Zirconia Sol-Gel Coating on Fracture Strength of Chemical Strengthened Soda Lime Glass

Lateral cracks in soda-lime glass under the threshold load due to the interaction of indentations

Scratch-induced micro-fracture behaviour and translational failure of glass: An experimental and numerical study

Chemical strengthening of high aluminosilicate glasses and experimental fitting

An Investigation into the Densification-Affected Deformation and Fracture in Fused Silica under Contact Sliding

Evaluation of crack initiation load of silica glass surfaces formed during subcritical crack growth

Lateral‐pushing induced surface lift‐up during nanoindentation of silicate glass

Nanoindentation‐induced evolution of atomic‐level properties in silicate glass: Insights from molecular dynamics simulations

Impact of strain rate on the Indentation Size Effect: Evidence of an intimate link between Size effect, Strain Rate and Ductility in Soda-lime Silica glass

Nanoindentation-induced evolution of atomic-level properties in silicate glass: Insights from molecular dynamics simulations

Sink-in/pile-up formation and crack nucleation mechanisms of high purity fused silica and soda-lime silica glass during nanoindentation experiments

Micro‐scale mechanical properties of surface layer in ion‐exchanged glass

Role of densification in deformation behaviors of model metallic glasses under 3-D nanoindentation studied in molecular dynamics simulation

Role of elastic deformation in determining the mixed alkaline earth effect of hardness in silicate glasses