Abstract:The present work investigated the influences of the variation of Si content and the minor amount of Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys systematically. Alloy compositions with Nb-21.6(Ti/Zr)-3.1Hf-(9.4–15.6)Si-6.3Cr-3.1Al-1.0B (at. %) were designed using a cluster formula approach to realize the substitution of similar elements, in which these alloys were solid-solutionized at 1573 K for 24 h and then aged at 1273 K for 24 h. It was found that all these aged alloys are mainly composed of BCC-Nb solid solution (Nbss), Nb 5 Si 3 and Cr 2 Nb phases, where the increase of Si content and the addition of Zr could significantly increase the volume fraction of Nb 5 Si 3 in a form of coarse and primary particles. Consequently, high-Si alloys possess outstanding mechanical property at high temperature, as evidenced by the fact that the yield strength ( σ YS = 373 MPa) at 1523 K of high-Si/Zr alloy containing 15.6 at. % Si and 1.6 at. % Zr is much higher than that ( σ YS = 266 MPa) of the low-Si alloy with 9.4 at. % Si and 0 Zr. It is mainly ascribed to the existence of primary Nb 5 Si 3 particles, besides the eutectic microstructure composed of Nbss and Nb 5 Si 3 , as well as fine Cr 2 Nb precipitates in Nbss. Moreover, a minor amount of Zr substitution for the Ti is conducive to the phase transition of α-Nb 5 Si 3 to γ-Nb 5 Si 3 . Thus, this high-Si/Zr alloy exhibits an improved oxidation resistance after 50 h-exposure at 1523 K, due to the lowest mass gain of about 80.9 mg/cm 2 . The constitutions of oxide scales in these alloys were characterized and compared, from which it was found that the better oxidation resistance is closely related to the formation of dense oxide scales. This work will provide a new approach to obtain an optimum combination of mechanical property and oxidation resistance of superalloys through multi-component alloying.

Mechanical Properties and Oxidation Behavior of Hot Pressing Sintered Nb5Cr Superalloy

Investigation of a Hot-Pressed Nb–Ti–Al Alloy: Mechanical Alloying, Microstructure and Mechanical Property

Microstructure and Mechanical Properties of the Powder Metallurgy Nb-16Si-24Ti-2Al-2Cr Alloy

Microstructure, Mechanical Properties and Oxidation Resistance of Nb-Si Based Ultrahigh-Temperature Alloys Prepared by Hot Press Sintering

Effect of Microstructure on High Temperature Mechanical Properties in Forming Ni-20cr-10mo-10co Superalloy

Effects of Heat Treatment on the Microstructure and Properties of a Cast Nickel-Based High-Cr Superalloy

The Effects of Alloying Elements Cr, Al, and Si on Oxidation Behaviors of Ni-Based Superalloys

Effects of Si variation and Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys

Optimization of the Microstructure and Mechanical Properties of a Laves Phase-Strengthened Hypoeutectic NiAl/Cr(Mo,W) Alloy by Suction Casting

Microstructure and Mechanical Properties of NiAl–Cr(Mo)/Nb Eutectic Alloy Prepared by Injection-Casting

Mechanical properties and microstructure evolution of NbSiZr based alloy

The high-temperature oxidation behavior and mechanism in a powder metallurgy Ni-based superalloy featuring δ-Nb3Al addition

Hot deformation behavior and hot working window of a solid solution strengthened Ni–Cr–Fe-based superalloy

Microstructure Evolution and Mechanical Properties of NiAlCrFeMo High Entropy Superalloy after Different Annealing Treatment

Microstructure Evolution and Mechanical Properties' Improvement of NiAl–Cr(Mo)–Hf Eutectic Alloy During Suction Casting and Subsequent HIP Treatment

Solidification behaviour and hot cracking susceptibility of a novel Ni-based superalloy

Effect of Heat Treatment on the Microstructure and Fracture Behaviors of a Ni–Cr–Fe Superalloy

Microstructure Characteristics and Compressive Properties of NiAl-based Multiphase Alloy During Heat Treatments

Microstructure and Thermal Deformation Behavior of Hot-Pressing Sintered Zr-6Al-0.1B Alloy

Effect of Heat Treatment on the Microstructure of Multiphase Nial-Based Alloy

Microstructure and mechanical properties of a new nickel-based single crystal superalloy