Abstract:Cu2O/CuO bilayers were fabricated by electrodeposition of the CuO layer in a copper(II)-ammonia complex aqueous solution, followed by photoelectrochemical deposition of the Cu2O layer at potentials ranging from -0.3 to -1.0 V referenced to a Ag/AgCl electrode in a copper(II)-lactate complex aqueous solution under light irradiation, and the effects of varied potentials of the photoelectrochemical Cu2O depositions and post-heating conditions on their structural, optical, and photovoltaic characteristics were investigated with X-ray diffraction, field emission-scanning electron microscopy, optical absorption measurements, and external quantum efficiency (EQE) measurements with and without applied bias voltage. The Cu2O layers with a characteristic 2.1 eV band gap energy were adhesively stacked on the thorn-like grains of the CuO layers possessing a characteristic 1.5 eV band gap energy, and dense and defect-free Cu2O/CuO bilayers could be fabricated at the potentials of -0.4 and -0.5 V, but the grain size of Cu2O decreased at -0.5 V. In addition, the metallic Cu was deposited simultaneously at potentials less than -0.7 V. The Cu2O/CuO bilayer fabricated at -0.4 V revealed photovoltaic features at wavelengths ranging from 350 nm to approximately 900 nm, and a maximum EQE value of 56.8% was achieved at 510 nm in wavelength with a bias voltage of -0.1 V. The maximum EQE value, however, decreased to 1.2% accompanied with the peak wavelength shift to 580 nm, and no photovoltaic feature was observed at potentials of -0.3, -0.7, and -1.0 V. The photovoltaic performance for the Cu2O/CuO bilayer fabricated at -0.4 V was ameliorated by heating at 423 K, and the maximum EQE values were enhanced to 87.7% at 550 nm and 89.8% at 530 nm in an ambient atmosphere and vacuum. Both the Cu2O and CuO layers acted as photovoltaic layers in the Cu2O/CuO bilayer fabricated at -0.4 V and heated at 423 K, and the electrical characteristic including the carrier mobility affected the photovoltaic performance. The photovoltaic feature, however, disappeared by heating above 523 K due to the formation of nanopores inside the CuO layer and near the CuO heterointerface to the Cu2O and fluorine-doped tin oxide substrate.

Structural and electrical properties of electrodeposited single junction of cuprous (I) oxide copper

CuBi2O4/CuO Heterojunction Coated with Electrodeposited ZnO Overlayer for Stable Solar Hydrogen Evolution

Microstructure, Morphology and Sunlight Response of Cuprous Oxide Thin Films

EPITAXIAL GROWTH OF CUPROUS OXIDE ELECTRODEPOSITED ONTO SEMICONDUCTOR AND METAL SUBSTRATES

In-Depth Study of Chemically Electrodeposited Cuprous Oxide (Cu2O) thin Films on ITO Glass

Epitaxil Electrodeposition Of A Crystalline Metal Oxide Onto Single-Crystalline Silicon

Electrodeposited Cu2O As Photoelectrodes with Controllable Conductivity Type for Solar Energy Conversion

Preparation of Cu2o/Zno P-N Junction by Thermal Oxidation Method for Solar Cell Application

Current Status and Future Prospects of Copper Oxide Heterojunction Solar Cells

Characterizations of Cuprous Oxide Thin Films Prepared by Sol-Gel Spin Coating Technique with Different Additives for the Photoelectrochemical Solar Cell

Epitaxial Electrodeposition of a Crystalline Metal Oxide onto Single-Crystalline Silicon

Electrochemically Deposited Cu2O on TiO2 Nanorod Arrays for Photovoltaic Application

Structure Defects and Photovoltaic Properties of TiO2:ZnO/CuO Solar Cells Prepared by Reactive DC Magnetron Sputtering

Interface-controlled Two-Dimensional Cuprous Oxide Structures

Quasi‐Single Crystalline Cuprous Oxide Wafers via Stress‐Assisted Thermal Oxidation for Optoelectronic Devices

Preparation Strategies of p-Type Cuprous Oxide and Its Solar Energy Conversion Performance

Optimizing the structure and optoelectronic properties of cuprite thin films via a plasma focus device as a solar cell absorber layer

Cu2O Homojunction Solar Cells: Efficiency Enhancement with a High Short Circuit Current

Inorganic Solar Cells Based on Electrospun ZnO Nanofibrous Networks and Electrodeposited Cu2O

Electrodeposition of Copper Oxides as Cost-Effective Heterojunction Photoelectrode Materials for Solar Water Splitting

Photoelctrochemically Fabricated and Heated Cu2O/CuO Bilayers with Enhanced Photovoltaic Characteristics