Abstract:The microstructure evolution of Inconel 740H during aging at 750°C for up to 3000h was investigated by means of optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), small-angle X-ray scattering (SAXS), three-dimensional atom probe (3DAP) analysis and micro-phase analysis. The mechanical properties of samples after aging were also studied. The grain size increased substantially during the whole aging period. Two different types of grain boundary carbides were observed; block-shaped and needle-shaped. Both were identified to be M23C6 by selected area diffraction measurements. The grain boundary carbides did not coarsen significantly during aging, with the weight fraction increasing only from 0.20% to 0.28%. In contrast, a much higher coarsening rate of γ′ precipitates was observed, as evidenced from both TEM observations and SAXS analysis. 3DAP was used to study the elemental partitioning behavior between γ′ precipitates and γ matrix as well as the evolution in width of the γ/γ′ interface. A large increase in the width of γ/γ′ interfaces was seen between 1000h and 3000h aging. In addition, for the sample aged at 750°C for 3000h, Cr enrichment on the γ matrix side of the γ/γ′ interface was found. Tensile tests at 750°C of the aged samples showed a gradual decrease in elevated-temperature yield strength after 500h, when this alloy was over-aged. The critical precipitate size for the transition from precipitate cutting by weakly coupled dislocations to strongly coupled dislocations for Inconel 740H was calculated to be approximately 50nm, which agrees well with the experiment measurements of elevated-temperature yield strength. The room temperature impact toughness of all samples decreased during aging as the grain size kept growing.

Microstructure evolution of Incoloy 800H in industrial environment and correlation with creep mechanisms from literature

Microstructure and Damage Evolution of Inconel 740H Welded Joint during Creep Process at 750 °C

Microstructure Evolution and Mechanical Properties of Inconel 740H During Aging at 750 °C

Experimental characterization of flat indentation creep behaviour of Inconel 617

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Creep Performance Study of Inconel 740H Weldment Based on Microstructural Deformation Mechanisms

In Situ SEM Study of Creep Deformation Behavior of Nickel-Based Single-Crystal Superalloys

Dynamic recrystallisation in Inconel®718 at creep conditions

Mechanisms of deformation, damage and life behavior of inconel 617 alloy during creep-fatigue interaction at 700 °C

Creep Behavior and Microstructure Evolution of Ni-based Alloy IN617 at 1000 °C

Microstructural Evolution of X20CrMoV12.1 Steel Upon Short-term Creep Rupture Test

Evaluation of Aged Incoloy 800 Alloy Sensitization to Intergranular Corrosion by Means of Double Loop Electrochemical Methods and Image Analysis

Creep Behaviors Evaluation of Incoloy800H by Small Punch Creep Test

Microstructure evolution and deformation mechanism of a [111]-oriented nickel-based single-crystal superalloy during high-temperature creep

Microstructural characterisation and microanalysis of creep resistant steels

Microstructure And Properties Of Welded Joint Of Incoloy800h Alloy By Tungsten Argon Arc Welding

Effect of Cold Rolling on Texture and Microstructure Development in Annealed Incoloy 800 Fabricated Using Selective Laser Melting

Investigation on the corrosion behavior of Alloy 800H at various levels of deformation

The Studies on Multiaxial Creep Behavior of Inconel 718 Notched Bar at 700 °C

The Experimental and Numerical Studies on Multiaxial Creep Behavior of Inconel 783 at 700 °C

Studies of High-Temperature Fatigue Behavior and Mechanism for Nickel-Based Superalloy Inconel 625