Abstract:In the multilayer film-substrate system, the buckling, delamination and cracking of the film caused by the thermal stress concentration point and the stress mutation are the main factors leading to the failure of the corresponding device function. In this paper, we studied the multilayer film system composed of the substrate and the three-layer film. The thermal stress distribution inside the structure was calculated by the finite element method (FEM). It was observed that there was a large thermal stress difference between the layers. This is mainly due to the mismatch of thermal expansion coefficient (CTE) between materials. Different materials have different degrees of change with the external environment temperature, and the layers are squeezed. In particular, there are obvious thermal stress concentration points at the corners of the base layer and the transition layer, which is due to the sudden change of the shape at the geometric section of the structure, resulting in a sudden increase in local stress. In order to solve this problem, we have chamfered the substrate and added an intermediate layer between the substrate and the transition layer to analyze whether the difference between the thermal stress concentration point and the thermal stress can be reduced or eliminated, and the service life of the multilayer structure can be extended. The conclusion shows that chamfering and increasing the intermediate layer can reduce the stress mutation and weaken the thermal stress concentration point, which can effectively improve the interlayer bonding strength.

Thermal stress concentration points and stress mutations in nano-multilayer film structures

Analysis of the Thermal Stress in Infrared Films

Elastic and elastic-plastic analysis of multilayer thin films filled with heterogeneous materials

Calculation of Thermal Stress in Microstructure Fabricated by Multilayer Thin Films

Optimum Designs for Multi-Layered Film Structures Based on the Knowledge on Residual Stresses

Overview and applicability of residual stress estimation of film–substrate structure

Fracture of Thermal Barrier Coating with Multiple Surface Cracks and Delaminations: Interlayer Effect

Thermal Stress Analysis of a Trilayer Film/substrate System with Weak Interfaces

Size-Dependent Analysis of Strain Energy Release Rate of Buckling Delamination Based on the Modified Couple Stress Theory

A Method of Studying the Effect of Stress and Thermal-stress Coupling on the Thermal Conductivity of the Film

Multiple cracking of thin films due to residual stress combined with bending stress

Size-Dependent Thermomechanical Responses of Nano-Sized Multilayers

Multiple Film Cracking in Film/substrate Systems with Mismatch Strain and Applied Strain

Study on the Crack Propagation of Stiff-Thin-Film-on-Soft-Substrate Structures under Biaxial Loading

Residual Stresses in the Elastoplastic Multilayer Thin Film Structures: the Cases of Si/Al Bilayer and Si/Al/Sio(2) Trilayer Structures

Thermal Mechanical Reliability of High Temperature Thermocouple Transducer with Composite Mul tilayer Film Structure

A Practical Approach for Determination of Thermal Stress and Temperature-Dependent Material Properties in Multilayered Thin Films

A Method for Testing Thermal Conductivity of Multi-layer Films

Stress in Film/substrate System Due to Diffusion and Thermal Misfit Effects

An Estimation Method on Failure Stress of Micro Thickness Cu Film-Substrate Structure

Micro 3D Measurement Applied to Interfacial Deformation of Bilayer Thin Film/substrate Structure under Thermal Cycling Loads