The development of biochar obtained from agricultural waste as a reducing agent in the ironmaking process
Ajcharapa Chuanchai,Keng-Tung Wu
DOI: https://doi.org/10.1007/s13399-024-06060-9
IF: 4.05
2024-08-29
Biomass Conversion and Biorefinery
Abstract:This study investigates the viability of employing biochar made from agricultural waste, such as mushroom cultivation waste (MR), specifically looking at its production under high carbonization temperatures and its ability to effectively reduce iron oxides. Through the optimization of the carbonization process, we were able to develop biochar that has a higher carbon content and reactivity to use as a reducing agent for the reduction process. The experimentation occurred in a batch multi-sectional temperature-controlled reactor spanning temperatures from 300 to 900 °C. In order to comprehensively assess the properties of biochar, we utilized a range of analytical instruments, such as the elemental analyzer (EA), Brunauer–Emmett–Teller (BET), thermogravimetric analyzer (TGA), X-ray fluorescence (XRF), and scanning electron microscopy (SEM) with energy-dispersive X-ray (EDX) analysis. As a result, with a carbonization temperature of 900 °C and a maximum fixed carbon content of 52.49 wt%, this biochar exhibits exceptional efficacy. In addition, the iron has a lowered sulfur level, which enhances its quality by reducing hardness and cracking. Moreover, at the initial stage, the feedstock has a specific surface area (SSA) of 0.874 m 2 /g and a total pore volume (TPV) of 0.004 cm 3 /g. Upon the application of heat, these values progressively rise, demonstrating significant increments, starting at 400 °C (SSA: 3.384 m 2 /g, TPV: 0.011 cm 3 /g) and even more drastically at 900 °C (SSA: 17.994 m 2 /g, TPV: 0.027 cm 3 /g). This study suggests the utilization of MR biochar, which is synthesized at a temperature of 700 °C, with a coke-to-biochar ratio of 20:80. It has been specifically identified as a suitable reducing agent for ironmaking processes at a temperature of 1300 °C for 20 min. This suitability is likely attributed to cost-effectiveness, energy efficiency, practical considerations, and a high metallization percentage. As a result, biochar is a practical and environmentally sustainable substance that can improve the sustainability and efficiency of the ironmaking process, therefore promoting the adoption of more environmentally friendly industrial practices.
energy & fuels,engineering, chemical