Abstract:Good gas permeability is an essential factor for the smooth operation and high performance in the lower part of the blast furnace. Under the present low carbon blast furnace smelting conditions, the coke layer is thinner, and the proportion of the molten metal in the coke layer is significantly higher, resulting in a major reduction in gas permeability, which seriously affects blast furnace operations. Also, the lower thickness of the coke layer weakens the process of solid-liquid carbon dissolution when the molten iron passes through the coke layer, which reduces the carbon content of the molten iron and further deepens the erosion of the refractory by the unsaturated molten iron. The carbon dissolution in the molten iron in a blast furnace core was measured by a high-temperature vacuum wettability test tool that analyzed the interface wetting activity between Fe−C melts with specific carbon mass fraction (3.8%, 4.3%, 4.8%) and 99.9% of high temperatures graphite plates. Besides, the scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the graphite substrate’s carburizing morphology and carburizing distances. The results show that, with the increase of carbon content, the interface contact angle becomes bigger. The contact angle decreases with time, and eventually reaches a steady-state during the melting process, and the Fe−C melt with saturated carbon cannot be wet. The scanning electron microscopy analysis shows that a spherical cap-like depression is created by a cross-section of the Fe−C melt and the graphite substrate, and the radius and volume of the depression decrease with increasing carbon content. The study of the EDS scanning analysis shows that the amount of dissolved carbon atoms in the graphite substrate penetrates the Fe−C melt and decreases with increasing initial carbon concentration. The smaller the carburizing effect, the better the wetting is conducive to carbon mass transfer. It is found that by measuring carburizing of the carbon atoms in the graphite substrate into the Fe−C melt by calculating the surface energy reduces the surface energy between the two. Thus, the surface tension decreases and the melt spreads slowly with contact angle gradually decreasing during melting.

Characterization and Reduction Behavior of Carbonized Ore Prepared by Iron Ore Immersion in Tar Derived from Biomass Pyrolysis

Investigation into Biomass Tar-Based Carbon Deposits as Reduction Agents on Iron Ore Using the Tar Impregnation Method

Porous Ore Structure and Deposited Carbon Type during Integrated Pyrolysis–Tar Decomposition

Effects of Iron Ores on the Pyrolysis Characteristics of a Low-Rank Bituminous Coal

Direct Reduction Ironmaking by Co-Pyrolysis of Biomass Tar Model Compounds and Iron Ore Fines

The Rate-Limiting Step in the Integrated Coal Tar Decomposition and Upgrading-Iron Ore Reduction Reaction Determined by Kinetic Analysis

Direct reduction of iron ore using biomass biochar: Reduction rate, microstructural and morphological analysis

Enhancement of Reduction Rate of Iron Ore by Utilizing Iron Ore/Carbon Composite Consisting of Fine Iron Ore Particles and Highly Thermoplastic Carbon Material

Carbothermal Reduction of Iron Ore in Its Concentrate-Agricultural Waste Pellets

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Effect of Ore Type and Gangue Content on Carburization and Melting Behavior of Carbon-Iron Ore Composite

Catalytic reforming of volatiles from co-pyrolysis of lignite blended with corn straw over three iron ores: Effect of iron ore types on the product distribution, carbon-deposited iron ore reactivity and its mechanism

Effect of Carbon Addition on Direct Reduction Behavior of Low Quality Magnetite Ore by Reducing Gas Atmosphere

Reduction of Iron‐Ore Pellets Using Different Gas Mixtures and Temperatures

Reduction Behavior and Mechanism of Iron Ore in Molten Iron in the Process of Converter Steelmaking

Potential of Pinewood Biochar as an Eco-Friendly Reducing Agent in Iron Ore Reduction

Reduction of Iron Oxide as an Oxygen Carrier by Coal Pyrolysis and Steam Char Gasification Intermediate Products

Effect of Pyrolysis Temperature on the Carbon Sequestration Capacity of Spent Mushroom Substrate Biochar in the Presence of Mineral Iron

Catalytic reforming of volatiles from co-pyrolysis of lignite blended with corn straw over three different structures of iron ores

Carbon Deposition and Sintering Characteristics on Iron-Based Oxygen Carriers in the Catalytic Cracking Process of Coal Tar

Insights into direct reduction iron using bamboo biomass as a green and renewable reducer: Reduction behavior study and kinetics analysis