Preparation and microwave absorption properties of Ni–Co nanoferrites
Bi-yu Chen,Ding Chen,Zhi-tao Kang,Ying-zhe Zhang
DOI: https://doi.org/10.1016/j.jallcom.2014.08.195
IF: 6.2
2015-01-01
Journal of Alloys and Compounds
Abstract:NixCo1−xFe2O4 (x=0.2, 0.5, 0.8) particles were prepared by a self-designed method, i.e., microwave assisted ball milling. A series of characterizations were carried out on the prepared powders, including X-ray Diffraction (XRD), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM) and vector network analyzer (VNA). XRD and TEM results indicated that the particles are well-crystallized and the average size is about 15nm. According to VSM results, the Ms values are 76emu/gm, 61emu/gm and 46emu/gm respectively, which obviously presented higher saturation magnetization values compared with other existing methods. Complex permittivity and permeability of Ni–Co ferrites were explored by VNA in the frequency of 2–18GHz, and the reflection loss (RL) was also calculated. The results illustrated that the minimum reflection loss values of the three ferrites all emerged in the range of 9–12GHz, and the Ni0.8Co0.2Fe2O4 with a thickness of 2.5mm could achieve −36.2dB at 11.52GHz, which indicated that the Ni–Co ferrite nanoparticles possessed great potential in microwave absorption applications.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering