Synthesis of niobium nitride porous nanofibers with excellent microwave absorption properties via reduction nitridation of electrospinning precursor nanofibers with ammonia gas
Yi Cui,Kaizheng Xu,Bin Zhu,Shilei Hu,Yuejun Chen,Dongfeng Lv,Yang Yu,Jinglong Bu,Hengyong Wei,Bo Liang
DOI: https://doi.org/10.1016/j.jallcom.2022.164453
IF: 6.2
2022-06-01
Journal of Alloys and Compounds
Abstract:In order to solve the pressing issue of electromagnetic interactions, such as radar detection, communications, information processing and transport originates from civil and military fields, the niobium nitride porous nanofibers as novel microwave absorption materials have been prepared by electrospinning method followed the ammonia reduction nitriding process in the present work. The chemical composition, phase composition and pore structure of niobium nitride fibers are related with the reduction nitriding temperature. It was found that the phase of as-prepared nanofibers was quadrate Nb4N5 phase and Nb5N6 phase formed with the increase of reduction nitriding temperature. Meanwhile, the O atoms were still existed in the form of NbNxOy solid solution. The XPS results also demonstrate that niobium nitride nanofibers had residual oxygen element and abundant valence state, which were positive to impedance matching and interface polarization. The nitrogen content increased and the oxygen content decreased with the increase of reduction nitriding temperature. It was verified that the fibers were composed of niobium nitride nano-crystallite and a large number of holes. The average size of niobium nitride nanoparticles and the pore diameter in nanofibers increase as the reduction nitriding temperature increases. The as-prepared niobium nitride nanofibers with characteristic porous fibrous structure would provide the outstanding conductivity loss, magnetic loss, Debye relaxation, multiple reflections and scatterings, and suitable impedance matching. Hereby, the niobium nitride porous nanofibers were synthesized at 800 ℃, it exhibited excellent electromagnetic wave absorption ability and its optimal reflection loss value was − 49.5 dB at 8.9 GHz when matching layer thickness was only 2.04 mm.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering