Abstract:Electrolytic manganese residue (EMR) is a solid filter residue obtained from manganese carbonate ore during the production of metal manganese. A potential avenue towards large-scale utilisation of EMR is its use in cement preparation. However, the preparation of cement materials using EMR requires high-temperature calcination. In this study, the thermal properties and pyrolysis kinetics of belite–calcium sulfoaluminate cement raw meal were systematically studied using a multiple-heating-rate method based on thermogravimetric analysis and a kinetic model. The kinetic and thermodynamic parameters was studied using non-isothermal Flynn–Wall–Ozawa (FWO), Kissinger–Akahira–Sunose (KAS), Friedman and Kissinger methods. The results showed that from 30 to 1300°C, the pyrolysis reaction of cement raw meal was mainly divided into four steps: the crystalline water removal from calcium sulphate dihydrate and bauxite, the ammonia nitrogen removal from ammonium salts and the calcium sulphate crystal transformation; the decomposition of calcium carbonate and carbon-containing organic matter; the sulphate and carbonate substance decomposition and the clinker mineral phase formation. The average activation energies calculated when using the non-isothermal FWO, KAS, Friedman and Kissinger methods were 244.49, 240.7, 239.24 and 380.60 kJ/mol and the average pre-exponential factors were 1.75 × 10 20 , 3.65 × 10 20 , 7.11 × 10 21 and 1.55 × 10 13 s −1 , respectively. Herein, the pyrolysis kinetics of the cement raw meal was divided into two main stages: In stage 1 ( α : 0.15–0.8, 524°C–754°C), the mechanism of P2/3 accelerated nucleation in the Mampel Power rule, and the reaction mechanism function was G( α )= α 3/2 . In stage 2 ( α : 0.80–0.95, 754°C–1165°C), during the local conversion of α = 0.2–0.8, when α was <0.5, the chemical reaction mechanism of the R3 phase boundary was noted and the mechanism function was G( α ) = 1 − (1− α ) 1/3 ; however, when α was >0.5, a random nucleation and subsequent growth mechanism of A6 was noted and the mechanism function was G( α ) = [−ln(1 − α )] 2/3 .

Low-Temperature Calcination of Belite-Calcium Sulphoaluminate Cement Clinker and the Hydration Process

Research on the Hydration Properties of C4A3S-CSH2 Cement System at Different Temperatures

Synthesis of high belite sulfoaluminate cement with high volume of mixed solid wastes

Utilization of Coal Gangue and Copper Tailings As Clay for Cement Clinker Calcinations

Preparation of Sulphoaluminate Cement Clinkers from Wet Flue Gas Desulphurized Slag

The performance of α′-belite calcium sulfoaluminate (C$A) cement preserved under SO 2 atmosphere compared to commercial products

Effect of Residual CaSO4 in Clinker on Properties of High Belite Sulfoaluminate Cement Based on Solid Wastes

Influence of Curing Temperature on the Performance of Calcined Coal Gangue-Limestone Blended Cements

Preparation and Hydration of Brownmillerite-Belite-Sulfoaluminate Cement

Effect of strontium slag on early hydration and mechanical properties of belite-C4A3$ cement

SYNTHESIS AND CHARACTERIZATION OF HIGH BELITE SULFOALUMINATE CEMENT THROUGH RICH ALUMINA FLY ASH AND DESULFURIZATION GYPSUM

Kinetic and thermodynamic analysis on preparation of belite-calcium sulphoaluminate cement using electrolytic manganese residue and barium slag by TGA

Microstructural characteristics of belite–sulfoaluminate cement clinkers with bottom ash

Hydrated Properties and Mineralogical Composition of Sulphoaluminate Cement Clinker Made from Red Mud

Coproduction of Belite Q-phase Cement Clinker in a Pulverized Coal Combustion Boiler and Its Hydration Performance

Effect of gypsum on hydration properties, composition and kinetics of low carbon belite-ye'elimite-Q phase-ferrite clinker

Influence of metakaolin and calcined montmorillonite on the hydration of calcium sulphoaluminate cement

Solutionizing of Additional Ions in Belite-Rich Clinkers and the Properties of the Resulting Cement

Synergistic use of electrolytic manganese residue and barium slag to prepare belite- sulphoaluminate cement study

Effect of polycarboxylate superplasticizer and calcium nitrite on the fluidity and early strength of belite sulfoaluminate cement

In situ powder diffraction study of belite sulfoaluminate clinkering