Abstract:Materials from theA2M3O12 family are known for their extensive chemical versatility while preserving the polyhedral-corner-shared orthorhombic crystal system, as well as for their consequent unusual thermal expansion, varying from negative and near-zero to slightly positive. The rarest are near-zero thermal expansion materials, which are of paramount importance in thermal shock resistance applications. Ceramic materials with chemistry Al2−xInxW3O12 (x = 0.2–1.0) were synthesized using a modified reverse-strike co-precipitation method and prepared into solid specimens using traditional ceramic sintering. The resulting materials were characterized by X-ray powder diffraction (ambient and in situ high temperatures), differential scanning calorimetry and dilatometry to delineate thermal expansion, phase transitions and crystal structures. It was found that the x = 0.2 composition had the lowest thermal expansion, 1.88 × 10−6 K−1, which was still higher than the end member Al2W3O12 for the chemical series. Furthermore, the AlInW3O12 was monoclinic phase at room temperature and transformed to the orthorhombic form at ca. 200 °C, in contrast with previous reports. Interestingly, the x = 0.2, x = 0.4 and x = 0.7 materials did not exhibit the expected orthorhombic-to-monoclinic phase transition as observed for the other compositions, and hence did not follow the expected Vegard-like relationship associated with the electronegativity rule. Overall, compositions within the Al2−xInxW3O12 family should not be considered candidates for high thermal shock applications that would require near-zero thermal expansion properties.

Phase transition and thermal expansion in W-substituted In2Mo3O12 ceramics

Sc- and W-substitution and Tuning of Phase Transition in the Al2Mo3O12

Phase transition temperature and negative thermal expansion of Sc-substituted In2(MoO4)3 ceramics

Double cation (KMg)3+ co-substitution to regulate negative thermal expansion property of ln2W3O12

Structural, in-situ Raman spectroscopy and XPS studies on ZrW2-Mo O8 ceramics with tunable negative thermal expansion properties

Phase Transition and Coefficients of Thermal Expansion in Al2−xInxW3O12 (0.2 ≤ x ≤ 1)

Negative Thermal Expansion Performance of (Namg)xcr2-X(moo4)3 X Cr 2-X (moo 4 ) 3 (0≤x≤1) ≤ X ≤ 1) Ceramics

Phase transition and negative thermal expansion of HfMnMo3O12

Phase Behaviors of the Zrmo2-Xwxo8 (X=0.2-2.0) System and the Preparation of an Mo-Rich Cubic Phase

Negative thermal expansion performance of (NaMg)xCr2-x(MoO4)3 (0≤x≤1) ceramics

Zr 1− X Yb X WMoO 8− X /2 ( X = 0, 0.04) Ceramics Fabricated by in Situ Synthesis from Trigonal Polymorph: Preparation, Sintering Process, and Negative Thermal Expansion Properties

Improving Room Temperature Negative Thermal Expansion Performance of Fe2‐xScx(MoO4)3

Controllable Thermal Expansion and Phase Transition in Yb2−xCrxMo3O12

Structure and Negative Thermal Expansion in Zr0.3Sc1.7Mo2.7V0.3O12

Effects of (KMg)3+ co-doping and sintering temperature on the negative thermal expansion property of Sc2W3O12 ceramics

Effects of (KMn)3+ substitution on phase transition and thermal expansion property of Fe2Mo3O12

Study of the Structures and Thermal Expansion Properties of Solid Solutions Yb2−xDyxW3O12 (0≤x≤1.5 and 1.8≤X≤2.0)

Composition Dependent Phase Transition and Its Induced Hysteretic Effect in the Thermal Conductivity of Wxmo1-Xte2

Composition and Temperature-Dependent Phase Transition in Miscible Mo1−xWxTe2 Single Crystals

Near-Zero Thermal Expansion and Phase Transitions in HfMg1- x Zn x Mo3O12

High configurational entropy for low phase transition temperature and thermal expansion of A2M3O12 oxide ceramics