Abstract:To improve the negative thermal expansion (NTE) performance of ln2W3O12, a novel series of NTE (KMg)xln2-xW3O12 ceramics were fabricated via the solid-state method. The effects of (KMg)3+ substitution on the phase composition, microstructure and thermal expansion property of the ln2W3O12 ceramics were characterized using X-ray diffraction (XRD), Raman spectrometer (Raman), X-ray photoelectron spectrometer (XPS), scanning electron microscopy (SEM), transmission electron microscope (TEM) and thermal mechanical analyzer (TMA). Results indicate that (KMg)3+ can partially replace In3+ in In2W3O12 and form a new phase KxMgxln2-xW3O12 with monoclinic symmetry. For x = 0.5, pure monoclinic (KMg)0.5ln1.5W3O12 ceramics is prepared and shows strong NTE. Its coefficient of thermal expansion is −7.89 × 10−6 °C−1 in 30–700 °C, in addition, no phase transition was observed over the entire testing temperature range. These research results indicate that double cations co-substitution is an effective strategy to improve the NTE property of ln2W3O12 through crystal structure modulation. This strategy could be extended to the performance modulation of other NTE materials.

Double cation (KMg)3+ co-substitution to regulate negative thermal expansion property of ln2W3O12