Abstract:Sisal fibers were extracted and treated in alkali solutions of varying pH concentrations to alter their physical properties for the study. The study explores the effect of the pH concentrations on the internal microstructure using computed tomography, the changes in fibers surface topography using laser confocal microscopy, and how the mechanical properties are affected regarding their surface topography and internal microstructure. The X-ray microscopy scans showed that the untreated fibers are hollow throughout their length, and when treated, these voids collapse and reduce the fibers' diameter. Moreover, this also showed that treatment affects the complete structure of the fiber. Where a pronounced degradation was observed at 25%. This also affects the overall fibers' surface topography and mechanical properties. Where optimal mechanical properties were reported at 1% alkali treatment, this is evidently supported by the change in surface topology at this concentration. This means optimal properties may be achieved at the alkali concentration range below 1% and not necessarily at higher concentrations. 在不同pH浓度的碱溶液中提取和处理剑麻纤维,以改变其物理性质,用于研究. 该研究使用计算机断层扫描探讨了pH浓度对内部微观结构的影响,使用激光共聚焦显微镜探讨了纤维表面形貌的变化,以及纤维表面形貌和内部微观结构对机械性能的影响. x射线显微镜扫描显示,未处理的纤维在整个长度上都是中空的,当处理时,这些空隙会坍塌并减小纤维的直径. 此外,这也表明处理会影响纤维的完整结构。在25%时观察到明显的降解. 这也会影响整个纤维的表面形貌和机械性能. 据报道,在1%的碱处理下获得了最佳机械性能,这显然得到了该浓度下表面拓扑结构变化的支持. 这意味着在低于1%的碱浓度范围内可以实现最佳性能,而不一定在更高的浓度下.

Impact of Alkali Treatment on the Internal Microstructure, Surface Topography and the Resulting Mechanical Properties of Single Sisal Fibers