Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

A new hexagonal AlZnY phase and the nano-hardness in Mg-Y-Al-Zn alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure And Mechanical Properties Of Mg-12.3zn-5.8y-1.4al Alloy

Effect of Zn and Y on microstructures and properties of normally-solidified Mg-Zn-Y alloys

Effect of Y on Age Hardening Response and Mechanical Properties of Mg-xY–1.5LPC −0.4zr Alloys

Microstructure, generation of intermetallic compounds and mechanical strengthening mechanism of as-cast Mg–4Y–xZn alloys

The Influence of Element Y on the Mechanical Properties of the As-Extruded Mg–Zn–Y–Zr Alloys

Effect of Y Concentration on the Microstructure and Mechanical Properties of As-Cast Mg–Zn–Y–Zr Alloys

Effects of Minor Y Addition on Microstructure and Mechanical Properties of Mg-Nd-Zn-Zr Alloy

Effect of W-phase on the Mechanical Properties of As-Cast Mg–Zn–Y–Zr Alloys

Intermetallic Phases in Mg–Co–Y Alloys

Microstructure and Precipitates in Mg-Zn-Y Alloys

A Near-bulk Quasicrystal Alloy Formed in Zn-Mg-Y System

Atomic-scale Insights on the Plate-Shaped Γ″ Phase in Mg–Gd–Y–Ag–Zr Alloy

Mechanical Properties and Yield Asymmetry of Mg-Y-Zn Alloys: Competitive Behavior of Second Phases

Microstructure and Phase Transformation of Forged Mg–3.7Zn–0.3Y–0.3Gd Quasicrystal Alloy

Orientation relationships between icosahedral clusters in hexagonal MgZn2 and monoclinic Mg4Zn7 phases in Mg-Zn(-Y) alloys

Quasicrystal-reinforced Mg alloys

Hot Compression Deformation Behavior of Mg-Zn-Al-(Y) Alloys Reinforced with Quasicrystal

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy