Abstract:In this study, a Ni 50.4 Ti 49.6 shape memory alloy (SMA) was fabricated by selective laser melting (SLM), and it is found that heat treatments were effective to change the phase transformation behavior, microstructure, and superelasticity under compression for SLM Ni 50.4 Ti 49.6 . Detailed results based on EBSD demonstrated that, for SLM Ni 50.4 Ti 49.6 during solid solution and aging (450 °C) treatment, the ultrafine cellular and columnar grains (∼16.5 μm) in as-fabricated Ni 50.4 Ti 49.6 became equiaxed grains (∼70.2 μm), and the frequency of low-angle grain boundaries (26.7%→13.5%) and kernel average misorientation (0.37 → 0.21) decreased. The SEM and TEM analyses show that Ti-rich Ti 2 Ni/Ti 4 Ni 2 O x and Ni-rich Ni 4 Ti 3 precipitate phases were formed in the matrix simultaneously. After solid solution treatment, the size and distribution of Ti 2 Ni/Ti 4 Ni 2 O x almost unchanged with aging temperature increasing from 350 °C to 550 °C, however, the size of Ni 4 Ti 3 in aging-treated NiTi samples increased with aging temperature obviously, and it is interesting to find that the distribution of Ni 4 Ti 3 became uneven and dislocation networks were formed in the matrix when the aging treatment reached up to 550 °C, which originated from the internal stress generated by supersaturated Ni atoms. Furthermore, the results of superelasticity for aging-treated NiTi demonstrated that the characteristics of Ni 4 Ti 3 precipitate phase were powerful to influence the process of superelasticity decay/fatigue instead of determining the ultimately recovery strain after 10 compressive cycles. The aging-treated NiTi with evenly-distributed, high-density, and relatively-small Ni 4 Ti 3 precipitate phase shows minimum recovery strain at 1st cycle compression and best superelasticity stability among three aging-treated NiTi, which was attributed to strong obstruction effect of these Ni 4 Ti 3 precipitate for the occurrence of stress-induced martensitic transformation process and formation of dislocations. In contrast, the aging-treated NiTi with unevenly-distributed and low-density Ni 4 Ti 3 precipitate shows maximum recovery strain at 1st cycle compression and worst superelasticity stability. These results in this work can bring some meaningful insights into tailoring the microstructure and superelasticity of SLM NiTi SMAs.

Effect of heat treatment on the microstructure and in-situ corrosion behavior of SLM-NiTi alloys

The effect of heat treatment on corrosion behavior of selective laser melted Ti-5Al-5Mo-5V-3Cr-1Zr alloy

Study on corrosion behavior of the selective laser melted NiTi alloy with superior tensile property and shape memory effect

Effect of heat treatment on the corrosion resistance behavior of selective laser melted Ti6Al4V ELI

Analysis of microstructure, mechanical properties, wear characteristics and corrosion behavior of SLM-NiTi under different process parameters

Effect of hot isostatic pressing on the mechanical and corrosive properties of Ti–Ni alloy fabricated by selective laser melting

Effect of heat treatment on the microstructure and superelasticity of NiTi alloy via selective laser melting

Corrosion Behavior of NiTi Alloys Fabricate by Selective Laser Melting Subjected to Femtosecond Laser Shock Peening

Effect of Heat Treatment on Microstructure and Mechanical Properties of a Selective Laser Melting Processed Ni-Based Superalloy GTD222

Corrosion Behavior on Orthopedic NiTi Alloy with Nanocrystalline/amorphous Surface

Effect of Volume Energy Density on Selective Laser Melting Niti Shape Memory Alloys: Microstructural Evolution, Mechanical and Functional Properties

Optimizing laser parameters and exploring building direction dependence of corrosion behavior in NiTi alloys fabricated by laser powder bed fusion

Effect of Subtransus Heat Treatment on the Microstructure and Mechanical Properties of Additively Manufactured Ti-6Al-4V Alloy

Effect of heat treatment on microstructure and mechanical properties of selective laser melted Inconel 718 alloy

Heat-treatment induced microstructural evolution and enhanced mechanical property of selective laser melted near β Ti-5Al-5Mo-5 V-3Cr-1Zr alloy

Effect of heat treatment on microstructure and functional properties of additively manufactured NiTi shape memory alloys

Effect of laser printing mode on surface topography, microstructure and corrosion property of additive manufactured NiTi alloy

Effect of heat treatment on the microstructure, mechanical properties and tribological behavior of Ti-45Nb alloy fabricated by laser powder bed fusion

Improved corrosion and long‐term immersion behavior in 3.5 wt% NaCl solution of laser powder bed fusion produced Ti5Cu after heat treatment

Effect of Post Processing Heat Treatment Routes on Microstructure and Mechanical Property Evolution of Haynes 282 Ni-Based Superalloy Fabricated with Selective Laser Melting (SLM)

Effect of subcritical-temperature heat treatment on corrosion of SLM SS316L with different process parameters