Effect of heat treatment on the microstructure and superelasticity of NiTi alloy via selective laser melting

H.Z. Lu,Z.J. Zhou,Y. Yang,R.C. Wang,H.W. Ma,W.S. Cai,D.Z. Zhu,C. Yang

DOI: https://doi.org/10.1016/j.jmrt.2024.03.148

IF: 6.267

2024-03-23

Journal of Materials Research and Technology

Abstract:In this study, a Ni 50.4 Ti 49.6 shape memory alloy (SMA) was fabricated by selective laser melting (SLM), and it is found that heat treatments were effective to change the phase transformation behavior, microstructure, and superelasticity under compression for SLM Ni 50.4 Ti 49.6 . Detailed results based on EBSD demonstrated that, for SLM Ni 50.4 Ti 49.6 during solid solution and aging (450 °C) treatment, the ultrafine cellular and columnar grains (∼16.5 μm) in as-fabricated Ni 50.4 Ti 49.6 became equiaxed grains (∼70.2 μm), and the frequency of low-angle grain boundaries (26.7%→13.5%) and kernel average misorientation (0.37 → 0.21) decreased. The SEM and TEM analyses show that Ti-rich Ti 2 Ni/Ti 4 Ni 2 O x and Ni-rich Ni 4 Ti 3 precipitate phases were formed in the matrix simultaneously. After solid solution treatment, the size and distribution of Ti 2 Ni/Ti 4 Ni 2 O x almost unchanged with aging temperature increasing from 350 °C to 550 °C, however, the size of Ni 4 Ti 3 in aging-treated NiTi samples increased with aging temperature obviously, and it is interesting to find that the distribution of Ni 4 Ti 3 became uneven and dislocation networks were formed in the matrix when the aging treatment reached up to 550 °C, which originated from the internal stress generated by supersaturated Ni atoms. Furthermore, the results of superelasticity for aging-treated NiTi demonstrated that the characteristics of Ni 4 Ti 3 precipitate phase were powerful to influence the process of superelasticity decay/fatigue instead of determining the ultimately recovery strain after 10 compressive cycles. The aging-treated NiTi with evenly-distributed, high-density, and relatively-small Ni 4 Ti 3 precipitate phase shows minimum recovery strain at 1st cycle compression and best superelasticity stability among three aging-treated NiTi, which was attributed to strong obstruction effect of these Ni 4 Ti 3 precipitate for the occurrence of stress-induced martensitic transformation process and formation of dislocations. In contrast, the aging-treated NiTi with unevenly-distributed and low-density Ni 4 Ti 3 precipitate shows maximum recovery strain at 1st cycle compression and worst superelasticity stability. These results in this work can bring some meaningful insights into tailoring the microstructure and superelasticity of SLM NiTi SMAs.

materials science, multidisciplinary,metallurgy & metallurgical engineering