High thermally stable dielectric permittivity, polarization enhancement and electrostrictive properties in Zr-substituted bismuth sodium titanate lead-free ferroelectric ceramics

Li Jin,Yunyao Huang,Jing Pang,Leiyang Zhang,Ruiyi Jing,Dong Guo,Hongliang Du,Xiaoyong Wei,Zhuo Xu,Xu Lu,Fangbin Wei,Gang Liu

DOI: https://doi.org/10.1016/j.ceramint.2020.06.062

IF: 5.532

2020-10-01

Ceramics International

Abstract:<p>Zr-substituted (Bi_0.5Na_0.5)(Ti_{1−<em>x</em>}Zr_<em>x</em>)O₃ (BNTZ) with <em>x</em> = 0.02–0.4 ceramics were prepared using solid-state reaction technique and their structural, dielectric and ferroelectric properties were investigated systematically. X-ray diffraction results suggest that Zr⁴⁺ ion can enter the (Bi_0.5Na_0.5)TiO₃ (BNT) crystal lattices at a limited value and a secondary phase appears in BNTZ ceramics when the <em>x</em> exceeds 0.1. Temperature-dependent dielectric permittivities of BNTZ ceramics show only one dielectric peak from room temperature to 500 °C for each composition, and this dielectric peak becomes broad gradually as <em>x</em> increases from 0.02 to 0.4. The permittivity of <em>x</em> = 0.4 varies less than ±10% between room temperature and 300 °C, indicating a superior thermal stability of the permittivity. Polarization enhancement is revealed by the polarization-electric field hysteresis loops and highest ferroelectric properties are obtained in <em>x</em> = 0.04. The electric-field-induced strains of <em>x</em> = 0.04 show a monotonous increase as temperature increases from 30 °C to 150 °C. At 80 kV/cm, a high strain level of 0.268% is achieved. Our results suggest that the introduction of Zr⁴⁺ ion could effectively tailor the dielectric and ferroelectric properties of BNT ceramics and <em>x</em> = 0.4 composition could find potential application in high temperature capacitor devices.</p>

materials science, ceramics