Thermal stability of dielectric and energy storage performances of Ca-substituted BNTZ ferroelectric ceramics

Yunyao Huang,Leiyang Zhang,Ruiyi Jing,Qingyuan Hu,D.O. Alikin,V. Ya Shur,Saikh Safiul Islam,Hongliang Du,Xiaoyong Wei,Guobao Feng,Lin Zhang,Li Jin

DOI: https://doi.org/10.1016/j.ceramint.2020.10.208

IF: 5.532

2021-03-01

Ceramics International

Abstract:In this study, we synthesized [Ca x (Bi0.5Na0.5)1−x ](Ti0 85Zr0.15)O3 (Ca-substituted BNTZ) ferroelectric ceramics with x = 0–0.15 using a solid-state reaction technique. The structural evolution of Ca-substituted BNTZ was revealed by X-ray diffraction combined with Rietveld crystal structure refinement. A pseudocubic structure with P4bm symmetry is suggested for all Ca-substituted BNTZ samples. Temperature-dependent dielectric properties show a clear and broad dielectric peak of approximately 340 °C. The dielectric peak becomes even wider, and the thermal stability of the permittivity is dramatically improved when x gradually increases. In the x = 0.10 composition, the permittivity at 25–450 °C varies between +5% and −14.5%. A recoverable energy storage density (W rec) of 2.79 J/cm3 with an energy storage efficiency (η) of 76% was achieved in the x = 0.07 composition, which suggests superior properties over other BNT-based systems. In addition, the compositions of x = 0.07, 0.10 and 0.15 show excellent thermal stability of W rec and η. This work proves that the thermal stability of dielectric and energy storage performances in BNT-based ferroelectric ceramics can be achieved by introducing ions without contributing to the polarization.

materials science, ceramics