Electrical properties of 0.94Bi<Subscript>0.5</Subscript>Na<Subscript>0.5</Subscript>TiO<Subscript>3</Subscript>–0.06Ba(Zr<Subscript>0.055</Subscript>Ti<Subscript>0.945</Subscript>)O<Subscript>3</Subscript> lead-free ceramics with high thermal stability

Jun-Jun Wang,Fei-Fei Guo,Bin Yang,Shan-Tao Zhang,Li-Mei Zheng,Feng-Min Wu,Wen-Wu Cao

DOI: https://doi.org/10.1007/s10854-017-8154-1

2018-01-01

Abstract:Here we report the 0.94(Bi0.5Na0.5)TiO3–0.06Ba(Zr0.055Ti0.945)O3 (0.94BNT–0.06BZT) lead-free ceramics was synthesized by two-step solid state reaction route. The structural, dielectric, ferroelectric, piezoelectric and electromechanical properties of the ceramics were studied, and showed excellent electric properties (P s  = 39.9 μC/cm2, P r  = 33.7 μC/cm2, E c  = 2.79 kV/mm, S = 0.20%, d 33  = 174 pC/N, k p = 0.33). The depolarization temperature (T d ) of the ceramics is about 65 °C, which is determined from the first hump of relative dielectric constant. The electromechanical factor k p disappears at 65 °C, is consistent with the depolarization temperature (T d ) and the ferroelectric-antiferroelectric phase transition temperature (T fe−afe ) determined from the temperature-dependent P–E and bipolar S–E curves. These results indicate the 0.94BNT–0.06BZT ceramics has a good thermal stability in range of − 60–60 °C, and meets the actual demand.