Abstract:The nitrogen doping (N-doping) treatment for niobium superconducting radio-frequency (SRF) cavities is one of the key enabling technologies that support the development of more efficient future large accelerators. However, the N-doping results have diverged due to a complex chemical profile under the nitrogen-doped surface. Particularly, under industrial-scale production conditions, it is difficult to understand the underlying mechanism thus hindering performance improvement. Herein, a combination of spatially resolved and surface-sensitive approaches is employed to establish the detailed near-surface phase composition of thermally processed niobium. The results show that intermediate phase segregations, particularly the nanometric carbon-rich phase, can impede the nitridation process and limit the interactions between nitrogen and the niobium sub-surface. In comparison, the removal of the carbon-rich layer at the Nb surface leads to enhanced nitrogen binding at the Nb surface. Combining the RF test results, it is shown that the complex uniformity and grain boundary penetrations of impurity elements have a direct correlation with the mid-field quench behavior in the N-doped Nb cavities. Therefore, proper control of the nanometric intermediate phase formation in discrete thermal steps is critical in improving the ultimate performance and production yield of the Nb cavities. The origin of the omnipresent mid-field quench issue of nitrogen-doped Nb cavities for modern electron accelerators is traced down to the nanometric phase compositions at the niobium surface by unraveling the key elemental interplay and functioning mechanisms of carbon, nitrogen, and oxygen. Guided by the findings, N-doped 1.3 GHz single-cell Nb cavity with top-tier performance is successfully manufactured.image

Simulation of Non-linear SRF losses derived from characteristic topography of etched and electropolished niobium surfaces

Contribution to mid-field Q slope in Niobium SRF cavities from linear RF loss mechanism due to topographic surface structures

The effect of niobium thin film structure on losses in superconducting circuits

Magnetic Field Dependent Microwave Losses in Superconducting Niobium Microstrip Resonators

A new first-principles calculation of field-dependent RF surface impedance of BCS superconductor and application to SRF cavities

Role of microstructure on flux expulsion of superconducting radio frequency cavities

Analysis of RF losses and material characterization of samples removed from a Nb3Sn-coated superconducting RF cavity

RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide

Fluxon-Induced Losses in Niobium Thin-Film Cavities Revisited

Sensitivity of Niobium Superconducting Cavities to Trapped Magnetic Flux Dissipation

Multi-mode Analysis of Surface Losses in a Superconducting Microwave Resonator in High Magnetic Fields

Nitrogen Contamination Causes High Field Q-Slope (HFQS) in Buffered Chemical Polished SRF Cavities

Influence of material parameters on the performance of niobium based superconducting RF cavities

Enhanced radio-frequency performance of niobium films on copper substrates deposited by high power impulse magnetron sputtering

Unraveling the Nanoscale Segregation Mechanism in N-Doped Niobium for Enhanced SRF Performance

Field-dependent nonlinear surface resistance and its optimization by surface nano-structuring in superconductors

A model to explain the Q-increase by moderate-temperature treatment in Nb SRF cavities

Analysis of post wet chemistry heat treatment effects on Nb SRF surface resistance

Finite Element Modeling of Electrochemical Polishing of Niobium in Hydrofluoric-Sulfuric Acid Electrolyte

Flux Expulsion and Material Properties of Niobium Explored in 644-650 MHz Cavities

Nanostructural features degrading the performance of superconducting radio frequency niobium cavities revealed by TEM and EELS