Abstract:We investigate the rf performance of several single-cell superconducting radio-frequency cavities subjected to low temperature heat treatment in nitrogen environment. The cavities were treated at temperature 120–165 °C for an extended period of time (24–48 h) either in high vacuum or in a low partial pressure of ultrapure nitrogen. The improvement in Q0 with a Q rise was observed when nitrogen gas was injected at ∼300 °C during the cavity cooldown from 800 °C and held at 165 °C , without any degradation in accelerating gradient over the baseline performance. The treatment was applied to several elliptical cavities with frequency ranging from 0.75 to 3.0 GHz, showing an improved quality factor as a result of low temperature nitrogen treatments. The Q rise feature is similar to that achieved by nitrogen alloying Nb cavities at higher temperature, followed by material removal by electropolishing. The surface modification was confirmed by the change in electronic mean free path and tuned with the temperature and duration of heat treatment. The decrease of the temperature-dependent surface resistance with increasing rf field, resulting in a Q rise, becomes stronger with increasing frequency and decreasing temperature. The data suggest a crossover frequency of ∼0.95 GHz above that the Q rise phenomenon occurs at 2 K. Some of these results can be explained qualitatively with an existing model of intrinsic field-dependence of the surface resistance with both equilibrium and nonequilibrium quasiparticle distribution functions. The change in the Q slope below 0.95 GHz may result from masking contribution of trapped magnetic flux to the residual surface resistance. https://doi.org/10.1103/PhysRevAccelBeams.27.062001 Published by the American Physical Society under the terms of the Creative Commons Attribution 4.0 International license. Further distribution of this work must maintain attribution to the author(s) and the published article's title, journal citation, and DOI. Published by the American Physical Society

A model to explain the Q-increase by moderate-temperature treatment in Nb SRF cavities

Study on the interstitial oxygen diffusion to understand the reduction of cryogenic RF loss for the superconducting radio-frequency niobium cavities

RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide

In-situ Synchrotron X-Ray Photoelectron Spectroscopy Study of Medium-Temperature Baking of Niobium for SRF Application

The Collaborative Effects of Intrinsic and Extrinsic Impurities in Low RRR SRF Cavities

Surface Resistance Effects of Medium Temperature Baking of Buffered Chemical Polished 1.3 GHz Nine-Cell Large-Grain Cavities

Analysis of post wet chemistry heat treatment effects on Nb SRF surface resistance

Field, frequency, and temperature dependencies of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

Advancement in the understanding of the field and frequency dependent microwave surface resistance of niobium

Effect of interstitial impurities on the field dependent microwave surface resistance of niobium

Oxide dissolution and oxygen diffusion scenarios in niobium and implications on the Bean–Livingston barrier in superconducting cavities

Field, frequency and temperature dependence of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities

Influence of Furnace Baking on Q-E Behavior of Superconducting Accelerating Cavities

A Path to Higher Q0 with Large Grain Niobium Cavities

Effective medium temperature baking of 1.3 GHz single cell SRF cavities

Correlation of srf performance to oxygen diffusion length of medium temperature heat treated cavities

On the quest of low temperature nitrogen infusion relevant for superconducting Nb based radio-frequency cavities

Enhancement in Quality Factor of SRF Niobium Cavities by Material Diffusion

Understanding the Mechanism of the Performance Improvement in Nitrogen-doped Niobium Superconducting Radio Frequency Cavity

Nanostructural features degrading the performance of superconducting radio frequency niobium cavities revealed by TEM and EELS

Improvement and protection of niobium surface superconductivity by atomic layer deposition and heat treatment