Si 3 N 4 Nanofibrous Aerogel with In Situ Growth of SiO x Coating and Nanowires for Oil/Water Separation and Thermal Insulation

Zongwei Tong,Baojie Zhang,Huijun Yu,Xiangjie Yan,Hui Xu,Xiaolei Li,Huiming Ji
DOI: https://doi.org/10.1021/acsami.1c05575
2021-05-05
Abstract:Nanofibrous aerogels constructed by ceramic fiber components (CNFAs) feature lightweight, compressibility, and high-temperature resistance, which are superior to brittle ceramic aerogels assembled from nanoparticles. Up to now, in order to obtain CNFAs with stable framework and multifunctionality such as hydrophobicity and gas absorption, it is necessary to perform binding and surface modification processes, respectively. However, the microstructure as well as properties of CNFAs are deteriorated by the direct addition of binders and modifiers. To tackle these problems, we introduced a unique low-temperature (100 °C) chemical vapor deposition method (LTCVD) to achieve the cross-linking and hydrophobization of Si<sub>3</sub>N<sub>4</sub> CNFA in only one step. More importantly, during the LTCVD process, SiO<sub><i>x</i></sub> coatings and nanowire arrays were in situ formed via vapor–solid (VS) and vapor–liquid–solid (VLS) mechanisms on the surface and intersection of Si<sub>3</sub>N<sub>4</sub> nanofibers, which cemented the aerogel framework, endowed it with hydrophobicity, and improved its oxidation resistance at high temperature. Compared to most of its counterparts, the Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA exhibited better mechanical properties, higher capability of oil/water separation (33–76 g·g<sup>–1</sup>), lower thermal conductivity (0.0157 W/m·K<sup>–1</sup>), and superior structural stability in a wide temperature range of −196–1200 °C. This work not only presents an excellent Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA for the first time but also provides fresh insights for the exquisite preparation strategy of CNFAs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c05575?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c05575</a>.Synthesis process of the MTMS/VTES xerogel and Si<sub>3</sub>N<sub>4</sub> nanofibers (Figure S1); fabrication of the Si<sub>3</sub>N<sub>4</sub> CNFA via directional freeze casting (Figure S2); illustration of the low-temperature CVD process and experimental setup (Figure S3); description of the growth mechanism of SiO<sub><i>x</i></sub> coating and SNAs (Figure S4); mechanical characterizations of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA (Figure S5); morphology of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA in radial direction (Figure S6); calculation of the Poisson's ratio of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA (Figure S7); demonstration of oil/water separation process (Figure S8); illustration of the measurement setup of ablation at under butane flame (Figure S9); XRD patterns, TEM images, and EDS mappings of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA after 30 min isothermal oxidation (Figure S10); comparison of different Si<sub>3</sub>N<sub>4</sub> insulation materials (Figure S11) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_001.pdf">PDF</a>)Axial compression and recovery processes of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA (movie S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_002.avi">AVI</a>)Radial compression and recovery processes of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA (movie S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_003.avi">AVI</a>)Demonstration of the compression and recovery processes using a 500 g weight (movie S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_004.avi">AVI</a>)Low-temperature hyperelasticity in liquid nitrogen (movie S4) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_005.avi">AVI</a>)High-temperature hyperelasticity in the flame of a butane blowtorch (movie S5) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_006.avi">AVI</a>)Demonstration of the hydrophobicity of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA (movie S6) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_007.avi">AVI</a>)Absorption process of dichloromethane (movie S7) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_008.avi">AVI</a>)Recycle process of Si<sub>3</sub>N<sub>4</sub>/SiO<sub><i>x</i></sub> CNFA by squeezing (movie S8) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_009.avi">AVI</a>)Repetitive absorption process of dichloromethane after squeezing (movie S9) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c05575/suppl_file/am1c05575_si_010.avi">AVI</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
What problem does this paper attempt to address?