Abstract:This article introduces an eco-friendly method for the reclamation of carbon fiber-reinforced polymers (CFRP). The research project involved numerous experiments using microwave-assisted pyrolysis (MAP) to explore a range of factors, such as the inert gas flow, the power level, the On/Off frequency of rotation, and the reaction duration. To design the experiments, the three-level Box-Behnken optimization tool was employed. To determine the individual and combined effects of the input parameters on the thermal decomposition of the resin, the data were analyzed using least-squares variance adjustment. The results demonstrate that the models developed in this study were successful in predicting the direct parameters of influence in the microwave-assisted decomposition of CFRPs. An optimal set of operating conditions was found to be the maximum nitrogen flow (2.9 L/min) and the maximum operating experimental power (914 W). In addition, it was observed that the reactor vessel's On/Off rotation frequency and that increasing the reaction time beyond 6 min had no significant influence on the resin elimination percentage when compared to the two other parameters, i.e., power and carrier gas flow rate. Consequently, the above-mentioned conditions resulted in a maximum resin elimination percentage of 79.6%. Following successful MAP, various post-pyrolysis treatments were employed. These included mechanical abrasion using quartz sand, chemical dissolution, thermal oxidative treatment using a microwave (MW) applicator and thermal oxidative treatment in a conventional furnace. Among these post-treatment techniques, thermal oxidation and chemical dissolution were found to be the most efficient methods, eliminating 100% of the carbon black content on the surface of the recovered carbon fibers. Finally, SEM evaluations and XPS analysis were conducted to compare the surface morphology and elementary constitution of the recovered carbon fibers with virgin carbon fibers.

Research on dynamic microwave low-temperature carbonization of high performance carbon fiber

Effect of Carbonization Temperature on Microwave Absorbing Properties of Polyacrylonitrile-Based Carbon Fibers

Decreasing the environmental impact of carbon fibre production via microwave carbonisation enabled by self-assembled nanostructured coatings

Microwave Treatment of Pre-Oxidized Fibers for Improving Their Structure and Mechanical Properties

Research on the recovery process and product performance of carbon fiber flexible sucker rod in microwave field

A Novel Method for Curing Carbon Fiber Reinforced Plastics by High-Pressure Microwave

Transformation of traditional carbon fibers from microwaves reflection to efficient absorption via carbon fiber microstructure modulation

Evaluation of Mechanical Properties and Pyrolysis Products of Carbon Fibers Recycled by Microwave Pyrolysis

Microwave Carbonization of Cotton Fiber for Production of Carbon Materials

Microwave Radiation Effects on Carbon Fibres Interfacial Performance

Strengthened microwave absorption properties of polymer-derived carbon-rich SiCN (Ni3Si) ceramic fibers pyrolyzed at low temperature

Optimization of a high-pressure microwave curing process for T800/X850 carbon fiber-reinforced plastic

Controlled fabrication and microwave absorption performance of cucurbit-like carbon nanofibers

Tailoring microstructures of carbon fiber reinforced carbon aerogel-like matrix composites by carbonization to modulate their mechanical properties and thermal conductivities

Effects of carbonization temperature on structure and mechanical strength of electrospun carbon nanofibrous mats

Pure Carbon Microwave Absorbers from Anion-Exchange Resin Pyrolysis

Microwave-Assisted Pyrolysis of Carbon Fiber-Reinforced Polymers and Optimization Using the Box-Behnken Response Surface Methodology Tool

Facile Synthesis of Tubular Magnetic Carbon Nanofibers by Hypercrosslinked Polymer Design for Microwave Adsorption

Microwave carbonization of cotton fiber for the production of carbon materials

Microwave Curing of Carbon Fiber/Bismaleimide Composite Laminates: Material Characterization and Hot Pressing Pretreatment

Microwave heating oxidative stabilization of KMnO4 modified polyacrylonitrile-based carbon fiber precursor