Ce–Si Mixed Oxide: A High Sulfur Resistant Catalyst in the NH 3 –SCR Reaction through the Mechanism-Enhanced Process
Wei Tan,Annai Liu,Shaohua Xie,Yong Yan,Thomas E. Shaw,Yu Pu,Kai Guo,Lulu Li,Shuohan Yu,Fei Gao,Fudong Liu,Lin Dong
DOI: https://doi.org/10.1021/acs.est.0c08410
2021-03-03
Abstract:Investigating catalytic reaction mechanisms could help guide the design of catalysts. Here, aimed at improving both the catalytic performance and SO<sub>2</sub> resistance ability of catalysts in the selective reduction of NO by NH<sub>3</sub> (NH<sub>3</sub>–SCR), an innovative CeO<sub>2</sub>–SiO<sub>2</sub> mixed oxide catalyst (CeSi2) was developed based on our understanding of both the sulfur poisoning and reaction mechanisms, which exhibited excellent SO<sub>2</sub>/H<sub>2</sub>O resistance ability even in the harsh working conditions (containing 500 ppm of SO<sub>2</sub> and 5% H<sub>2</sub>O). The strong interaction between Ce and Si (Ce–O–Si) and the abundant surface hydroxyl groups on CeSi2 not only provided fruitful surface acid sites but also significantly inhibited SO<sub>2</sub> adsorption. The NH<sub>3</sub>–SCR performance of CeSi2 was promoted by an enhanced Eley–Rideal (E–R) mechanism in which more active acid sites were preserved under the reaction conditions and gaseous NO could directly react with adsorbed NH<sub>3</sub>. This mechanism-enhanced process was even further promoted on sulfated CeSi2. This work provides a reaction mechanism-enhanced strategy to develop an environmentally friendly NH<sub>3</sub>–SCR catalyst with superior SO<sub>2</sub> resistance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.0c08410?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.0c08410</a>.Information about catalytic performance tests; catalyst characterizations; texture properties; NH<sub>3</sub>–SCR activity of recently reported catalysts in presence of SO<sub>2</sub> and H<sub>2</sub>O; BET surface areas; fitting results of EXAFS oscillations for CeSi2 and CeO<sub>2</sub>; surface atomic concentrations and Ce<sup>3+</sup> ratios of CeSi2, Ce/2Si, and CeO<sub>2</sub>; fitting results of XANES spectra of CeSi2 and CeO<sub>2</sub>; NH<sub>3</sub> oxidation activity of CeSi2, Ce/2Si, and CeO<sub>2</sub>; NH<sub>3</sub>–SCR performance of CeSi2 and Ce/2Si cycling test; TG plots of fresh and used CeO<sub>2</sub>, Ce/2Si, and CeSi2; SO<sub>2</sub>-TPD profiles of CeO<sub>2</sub> and CeSi2; H<sub>2</sub>-TPR profiles of fresh and used CeO<sub>2</sub>, Ce/2Si, and CeSi2; NH<sub>3</sub>–SCR activity of Cu-SSZ-13 and V<sub>2</sub>O<sub>5</sub>–WO<sub>3</sub>/TiO<sub>2</sub>; elemental mapping images of Ce/2Si and CeSi2; XANES spectra of Ce L<sub>3</sub> edge for CeO<sub>2</sub> and CeSi2; <i>in situ</i> DRIFTS of NH<sub>3</sub> adsorption–desorption on CeSi2; and NO-TPD profiles of CeO<sub>2</sub> and CeSi2 (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.0c08410/suppl_file/es0c08410_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
environmental sciences,engineering, environmental